Immobilized glucose oxidase on magnetic silica and alumina: Beyond magnetic separation.

Here we report immobilization of glucose oxidase (GOx) on magnetic silica (Fe3O4-SiO2) and alumina (Fe3O4-Al2O3) functionalized with amino groups using glutaraldehyde as a linker. Magnetic support based biocatalysts demonstrate high catalytic activity in d-glucose oxidation to D-gluconic acid at pH 5-7.5 and temperature of 30-50 °C with the best activities of 95% and 91% for magnetic silica and alumina, respectively. A comparison of magnetic and non-magnetic alumina and silica shows a significant enhancement of the relative catalytic activity for magnetic supports, while the silica based biocatalysts show a higher activity than the biocatalysts based on alumina. A noticeably higher activity of GOx immobilized on magnetic supports is explained by synergy of the GOx inherent activity and enzyme-like activity of iron oxide nanoparticles, while the enhancement with silica based catalysts is most likely due to a larger pore size and stronger Brønsted acid sites. Excellent relative activity of Fe3O4-SiO2-GOx (95% of native GOx) in a tolerant pH and temperature range as well as high stability in a repeated use (6% relative activity loss after five catalytic cycles) makes this catalyst promising for practical applications.

Metal-Ion Distribution and Oxygen Vacancies That Determine the Activity of Magnetically Recoverable Catalysts in Methanol Synthesis.

Here, we report on the development of novel Zn-, Zn-Cr-, and Zn-Cu-containing catalysts using magnetic silica (Fe3O4-SiO2) as the support. Transmission electron microscopy, powder X-ray diffraction, and X-ray photoelectron spectroscopy (XPS) showed that the iron oxide nanoparticles are located in mesoporous silica pores and the magnetite (spinel) structure remains virtually unchanged despite the incorporation of Zn and Cr. According to XPS data, the Zn and Cr species are intermixed within the magnetite structure. In the case of the Zn-Cu-containing catalysts, a separate Cu2O phase was also observed along with the spinel structure. The catalytic activity of these catalysts was tested in methanol synthesis from syngas (CO + H2). The catalytic experiments showed an improved catalytic performance of Zn- and Zn-Cr-containing magnetic silicas compared to that of the ZnO-SiO2 catalyst. The best catalytic activity was obtained for the Zn-Cr-containing magnetic catalyst prepared with 1 wt % Zn and Cr each. X-ray absorption spectroscopy demonstrated the presence of oxygen vacancies near Fe and Zn in Zn-containing, and even more in Zn-Cr-containing, magnetic silica (including oxygen vacancies near Cr ions), revealing a correlation between the catalytic properties and oxygen vacancies. The easy magnetic recovery, robust synthetic procedure, and high catalytic activity make these catalysts promising for practical applications.