Defect stabilization in ZnO nanorods by Mg2+ doping.

Luminescent ZnO and Zn0.95Mg0.05O nanorods with length around 0.5 to 3 microm and diameter 100-150 nm were prepared by a facile solvothermal method. On hydriding at room temperature, a change of morphology from nanorods with aspect ratio 5-10 to particles of sizes 100 nm has been observed in both ZnO and Zn0.95Mg0.05O. While hydrided Zn0.95Mg0.05O showed an enhanced defect related green emission, the same got suppressed in hydrided ZnO. Even though it is observed that zinc vacancies are present in both as prepared ZnO and Zn0.95Mg0.05O, luminescence studies indicate that zinc vacancies get stabilized in Zn0.95Mg0.05O on hydrogenation.

Possible weak ferromagnetism in pure and M (Mn, Cu, Co, Fe and Tb) doped NiGa2O4 nanoparticles.

We report on the structural and magnetic properties of nanoparticles of NiGa2O4 and 5 at.% M doped (M = Mn2+, Cu2+, Co2+, Fe3+ and Tb3+) at Ga site of NiGa2O4, synthesized by gel-combustion method. The particle size, as investigated by X-ray diffraction and transmission electron microscopy, could be fine tuned by a controlled annealing process. Weak ferromagnetism becomes significant, when the particles are in the nano regime (5-7 nm). The magnetization becomes insignificant at larger particle size ( 150 nm). Cu2+ and Tb3+ doped NiGa2O4 nanoparticles showed relatively large room temperature ferromagnetism compared to other doped (Fe, Mn and Co) and undoped NiGa2O4 samples. The weak ferromagnetism observed in the nanoparticles of NiGa2O4, which is antiferromagnetic in the bulk, is due to the surface disordered states with uncompensated spins.