ABSTRACT
We demonstrate a compact, room-temperature, cw Yb(3+):Y(3)Al(5)O(12) silica (Yb(3+):YAG silica) fiber laser grown by the codrawing laser-heated pedestal growth technique. A slope efficiency of 76.3% was achieved from a 7 mm Yb(3+):YAG silica fiber, corresponding to an extracted power of nearly 1 W/cm. A laser side-mode suppression ratio of 70 dB was obtained with a 3 dB linewidth of 0.15 nm. Additionally, the propagation loss and emission cross section were determined by analyzing the lasing thresholds and slope efficiencies.
ABSTRACT
We report what we believe to be the first demonstration of a room-temperature, continuous-wave Cr(4+):Y(3)Al(5)O(12) (Cr(4+):YAG) double-clad crystal fiber laser grown by the codrawing laser heated pedestal growth method. The threshold is below 100 mW, which is a factor of 4 lower than previously reported Cr(4+)-doped lasers. A slope efficiency of 6.9% was obtained, and is in good agreement with the numerical simulation. In additional to small core diameter, the low-threshold lasing is made possible by the low propagation loss of 0.08 dB/cm and the high crystallinity of the core.