ABSTRACT
Recently, material extrusion (MEX) 3D printing technology has attracted extensive attention. However, some high-performance thermoplastic polymer resins, such as polycarbonate (PC), cannot be processed by conventional MEX printing equipment due to poor processing performance. In order to develop new PC-based printing materials suitable for MEX, PC/poly(butylene adipate-co-terephthalate) (PBAT) blends were prepared using a simple polymer blending technique. It was found that the addition of PBAT component significantly improved processing performance of the PC, making the blends processable at 250 °C. More importantly, the PC was completely compatible with the PBAT, and the PBAT effectively reduced the Tg of the blends, endowing the blends with essential 3D printing performance. Furthermore, methyl methacrylate-butadiene-styrene terpolymer (MBS) was introduced into the PC/PBAT blends to improve toughness. SEM observations demonstrated that MBS particles, as stress concentration points, triggered shear yielding of polymer matrix and absorbed impact energy substantially. In addition, the MBS had little effect on the 3D printing performance of the blends. Thus, a PC/PBAT/MBS blend system with favorable comprehensive mechanical properties and 3D printing performance was achieved. This work can provide guidance for the development of novel MEX printing materials and is of great significance for expanding the variety of MEX printing materials.
ABSTRACT
In this work, 3D printed polylactic acid (PLA)/polycaprolactone (PCL) nanocomposites with favorable thermo-responsive cyclic shape memory effects (SMEs) and crystallization and mechanical properties were fabricated using a two-step method. First, an isocyanate-terminated PCL diol (PCL-NCO) was synthesized through the reaction between isocyanate groups of hexamethylene diisocyanate and active hydroxyl groups of PCL diol, and its physicochemical properties were characterized. A PLA/PCL blend with a PCL content of 50 wt% was fabricated via fused filament fabrication (FFF) 3D printing, and the influence of the PCL-NCO on the SME of the PLA/PCL blend was studied. The results indicated that the PCL-NCO significantly improved the cyclic shape memory performance of 3D printed PLA/PCL blends and was proved to be an effective interface compatibilizer for the blend system. Subsequently, the structure and properties of 3D printed PLA/PCL nanocomposites were investigated in detail by adding cellulose nanocrystal-organic montmorillonite (CNC-OMMT) hybrid nanofillers with different contents. It was found that the hybrid nanofillers greatly enhanced crystallization and mechanical properties of the nanocomposites due to adequate dispersion. The modification of the PLA/PCL blend and the preparation of the 3D printed nanocomposite can not only prolong the service life of a shape memory polymer product, but also broaden its application scope in advanced fields.