ABSTRACT
Mixed Sn-Pb perovskites have emerged as promising photovoltaic materials for both single- and multi-junction solar cells. However, achieving their scale-up and practical application requires further enhancement in stability. We identify that their poor thermal conductivity results in insufficient thermal transfer, leading to heat accumulation within the absorber layer that accelerates thermal degradation. A thermal regulation strategy by incorporating carboranes into perovskites is developed; these are electron-delocalized carbon-boron molecules known for their efficient heat transfer capability. We specifically select ortho-carborane due to its low thermal hysteresis. We observe its existence through the perovskite layer showing a decreasing trend from the buried interface to the top surface, effectively transferring heat and lowering the surface temperature by around 5 °C under illumination. o-CB also facilitates hole extraction at the perovskite/PEDOT:PSS interface and reduces charge recombination. These enable mixed Sn-Pb cells to exhibit improved thermal stability, retaining 80% of their initial efficiencies after aging at 85 °C for 1080 hours. When integrated into monolithic all-perovskite tandems, we achieve efficiencies of over 27%. A tandem cell maintains 87% of its initial PCE after 704 h of continuous operation under illumination.
ABSTRACT
The rapid relaxation of hot carriers leads to energy loss in the form of heat and consequently restricts the theoretical efficiency of single-junction solar cells; However, this issue has not received much attention in tin-lead perovskites solar cells. Herein, tin(II) oxalate (SnC2O4) is introduced into tin-lead perovskite precursor solution to regulate hot-carrier cooling dynamics. The addition of SnC2O4 increases the length of carrier diffusion, extends the lifetime of carriers, and simultaneously slows down the cooling rate of carriers. Furthermore, SnC2O4 can bond with uncoordinated Sn2+ and Pb2+ ions to regulate the crystallization of perovskite and enable large grains. The strongly reducing properties of the C2O4 2- can inhibit the oxidation of Sn2+ to Sn4+ and minimize the formation of Sn vacancies in the resulting perovskite films. Additionally, as a substitute for tin(II) fluoride, the introduction of SnC2O4 avoids the carrier transport issues caused by the aggregation of F- ions at the interface. As a result, the SnC2O4-treated Sn-Pb cells show a champion efficiency of 23.36%, as well as 27.56% for the all-perovskite tandem solar cells. Moreover, the SnC2O4-treated devices show excellent long-term stability. This finding is expected to pave the way toward stable and highly efficient all-perovskite tandem solar cells.
ABSTRACT
The migration of ions is known to be associated with various detrimental phenomena, including current density-voltage hysteresis, phase segregation, etc., which significantly limit the stability and performance of perovskite solar cells, impeding their progress toward commercial applications. To address these challenges, we propose incorporating a polymerizable organic small molecule monomer, N-carbamoyl-2-propan-2-ylpent-4-enamide (Apronal), into the perovskite film to form a crosslinked polymer (P-Apronal) through thermal crosslinking. The carbonyl and amino groups in Apronal effectively interact with shallow defects, such as uncoordinated Pb2+ and iodide vacancies, leading to the formation of high-quality films with enhanced crystallinity and reduced lattice strain. Furthermore, the introduction of P-Apronal improves energy level alignment, and facilitates charge carrier extraction and transport, resulting in a champion efficiency of 25.09 %. Importantly, P-Apronal can effectively suppress the migration of I- ions and improve the long-term stability of the devices. The present strategy sets forth a path to attain long-term stability and enhanced efficiency in perovskite solar cells.
ABSTRACT
High-performance perovskite solar cells have demonstrated commercial viability, but still face the risk of contamination from lead leakage and long-term stability problems caused by defects. Here, an organic small molecule (octafluoro-1,6-hexanediol diacrylate) is introduced into the perovskite film to form a polymer through in situ thermal crosslinking, of which the carbonyl group anchors the uncoordinated Pb2+ of perovskite and reduces the leakage of lead, along with the -CF2 - hydrophobic group protecting the Pb2+ from water invasion. Additionally, the polymer passivates varieties of Pb-related and I-related defects through coordination and hydrogen bonding interactions, regulating the crystallization of perovskite film with reduced trap density, releasing lattice strain, and promoting carrier transport and extraction. The optimal efficiencies of polymer-incorporated devices are 24.76 % (0.09â cm2 ) and 20.66 % (14â cm2 ). More importantly, the storage stability, thermal stability, and operational stability have been significantly improved.