ABSTRACT
We have investigated the mechanical properties of neutron irradiated Czochralski (NICZ) silicon using nanoindentations combined with micro-Raman spectroscopy. It is found that NICZ silicon shows higher hardness (â¼13% higher) than non-irradiated silicon, with a slightly lower Young's modulus. When the samples were subjected to isochronal anneals in the temperature range of 250 °C-650 °C, the hardness of NICZ silicon gradually decreases as the temperature increases and it is finally comparable to that of the non-irradiated silicon. The vacancies and vacancy-oxygen defects induced by neutron irradiation in NICZ silicon annihilate or transform into more complex defects during the annealing processes. It suggests that the vacancy defects play a role in the evolution of hardness, which promote phase transition from the Si-I phase to the stiffer Si-II phase in NICZ silicon during indentation. In addition, the irradiation induced vacancy defects could lead to the lower Young's modulus.