Deformation Rate-Adaptive Conducting Polymers and Composites.

Materials are more easily damaged during accidents that involve rapid deformation. Here, a design strategy is described for electronic materials comprised of conducting polymers that defies this orthodox property, making their extensibility and toughness dynamically adaptive to deformation rates. This counterintuitive property is achieved through a morphology of interconnected nanoscopic core-shell micelles, where the chemical interactions are stronger within the shells than the cores. As a result, the interlinked shells retain material integrity under strain, while the rate of dissociation of the cores controls the extent of micelle elongation, which is a process that adapts to deformation rates. A prototype based on polyaniline shows a 7.5-fold increase in ultimate elongation and a 163-fold increase in toughness when deformed at increasing rates from 2.5 to 10 000% min-1 . This concept can be generalized to other conducting polymers and highly conductive composites to create "self-protective" soft electronic materials with enhanced durability under dynamic movement or deformation.

3D printed architected conducting polymer hydrogels.

Conducting polymer hydrogels combine electrical conductivity and tunable water content, rendering them strong candidates for a range of applications including biosensors, cell culture platforms, and energy storage devices. However, these hydrogels are mechanically brittle and prone to damage, prohibiting their use in emerging applications involving dynamic movement and large mechanical deformation. Here, we demonstrate that applying the concept of architecture to conducting polymer hydrogels can circumvent these impediments. A stereolithography 3D printing method is developed to successfully fabricate such hydrogels in complex lattice structures. The resulting hydrogels exhibit elastic compressibility, high fracture strain, enhanced cycling stability, and damage-tolerant properties despite their chemical composition being identical to their brittle, solid counterparts. Furthermore, concentrating the deformation to the 3D geometry, rather than polymer microstructure, effectively decouples the mechanical and electrical properties of the hydrogel lattices from their intrinsic properties associated with their chemical composition. The confluence of these new physical properties for conducting polymer hydrogels opens broad opportunities for a myriad of dynamic applications.

Synthesis of N = 8 Armchair Graphene Nanoribbons from Four Distinct Polydiacetylenes.

We demonstrate a highly efficient thermal conversion of four differently substituted polydiacetylenes (PDAs 1 and 2a-c) into virtually indistinguishable N = 8 armchair graphene nanoribbons ([8]AGNR). PDAs 1 and 2a-c are themselves easily accessed through photochemically initiated topochemical polymerization of diynes 3 and 4a-c in the crystal. The clean, quantitative transformation of PDAs 1 and 2a-c into [8]AGNR occurs via a series of Hopf pericyclic reactions, followed by aromatization reactions of the annulated polycyclic aromatic intermediates, as well as homolytic bond fragmentation of the edge functional groups upon heating up to 600 °C under an inert atmosphere. We characterize the different steps of both processes using complementary spectroscopic techniques (CP/MAS 13C NMR, Raman, FT-IR, and XPS) and high-resolution transmission electron microscopy (HRTEM). This novel approach to GNRs exploits the power of crystal engineering and solid-state reactions by targeting very large organic structures through programmed chemical transformations. It also affords the first reported [8]AGNR, which can now be synthesized on a large scale via two operationally simple and discrete solid-state processes.