Interferência dos métodos de fotopolimerização na microinfiltração marginal de restaurações de resina composta / Interference of the light cure methods in the marginal microleakage of restorations of composed resin

Avaliou-se o selamento marginal de restaurações de resina composta em dentes bovinos empregando-se o teste de microinfiltração, variando-se a fotopolimerização. Sessenta dentes receberam preparos cavitários, tipo “caixa” e a seguir, foram divididos em 5 grupos de 12 dentes cada. Após ataque ácido, e aplicação do adesivo Single Bond-3M ESPE, os dentes foram restaurados com a resina composta Z250-3M ESPE, em 2 incrementos, variando-se as fotopolimerizações: grupo 1: 600mW/cm²/30s com um aparelho XL3000-3M ESPE; o grupo 2: 180mW/cm²/10s com a ponta do fotopolimerizador à 14mm de distância da restauração, repouso por 10s e depois por 20s com a ponta do fotopolimerizador em contato com a resina, grupo 3 com um aparelho progressivo – Jet Lite 4000 Plus – J.Morita de 100 a 1400 mW/cm², por 30s, grupo 4 com um aparelho de Led – Led-Lec – MM Optics de potência de 130 mW/cm² e o grupo 5 com um Led para clareamento Bright Lec II de 600 mW/cm². Os dentes foram termociclados por 500 ciclos, (5ºC-55ºC), submersos em solução de nitrato de prata 50% por 24 horas, lavados por 20min e colocados em solução reveladora de radiografias por 8 horas. Os dentes foram seccionados e as imagens coletadas por uma câmera digital acoplada a um estereomicroscópio e analisadas através do programa computacional Image Tool 3.0. Após aplicar os testes ANOVA e de Tukey (5%), concluímos que o Jet Lite apresentou os maiores valores de microinfiltração marginal estaticamente significante e que os demais grupos não apresentam diferenças significantes, compondo o seguinte ranking decrescente de valores de microinfiltração marginal:Bright Lec>convencional>distância>Led-lec.

Influence of cavity preparation and curing method on the marginal seal of resin composite restorations: an in vitro evaluation.

OBJECTIVE: To evaluate the influence of cavity design and photocuring method on the marginal seal of resin composite restorations. METHOD AND MATERIALS: Seventy-two bovine teeth were divided into 2 groups: group 1 received box-type cavity preparations, and group 2 received plate-type preparations. Each group was divided into 3 subgroups. After etching and bonding, Z250 resin composite (3M Espe) was applied in 2 equal increments and cured with 1 of 3 techniques: (1) conventional curing for 30 seconds at 650 mW/cm2; (2) 2-step photocuring, in which the first step was performed 14 mm from the restoration for 10 seconds at 180 mW/cm2 and the second step was performed in direct contact for 20 seconds at 650 mW/cm2; or (3) progressive curing using Jetlite 4000 (J. Morita) for 8 seconds at 125 mW/cm2 and then 22 seconds at 125 mW/cm2 up to 500 mW/cm2. The specimens were thermocycled for 500 cycles and then submitted to dye penetration with a 50% silver nitrate solution. Microleakage was assessed using a stereomicroscope. Data were analyzed using analysis of variance and Tukey test (5% level of significance). RESULTS: A statistically significant difference was found between groups when a double interaction between photocuring and cavity preparation was considered (P = .029). CONCLUSIONS: No one type of cavity preparation or photocuring method prevented micro-leakage. The plate-type preparation showed the worst dye penetration when conventional and progressive photocuring methods were used. The best results were found using the 2-step photocuring with the plate-type preparation.

Odontogeriatria: sugestão de um programa de prevenção / Geriatric dentistry: suggestion of a prevention program

Os autores procuram evidenciar a necessidade e a viabilidade de promover saúde bucal, no idoso através da prevenção, uma vez que este grupo etário vem sofrendo muitas mudanças em seu perfil, com o aumento em número de indivíduos e melhoria de suas condições bucais, que se deve a uma conscientização da necessidade da manutenção dos dentes, seja pela função ou pela estética, que é uma imposição da sociedade atual. Através de orientação, material de higienização adequado, e principalmente a motivação do idoso através de sua auto estima, conseguiu-se resultados satisfatórios com esse trabalho