ABSTRACT
A multi-analytical approach was used to investigate the effect of thermal aging on the microstructure and mechanical properties of ER308L/Z2CND18.12N2. The results demonstrated that fractures occurred preferentially on the ER308L side. Z2CND18.12N2 exhibited superior fracture toughness compared to ER308L regardless of thermal aging time. The ultimate tensile strength significantly increased from 564.5 MPa in the unaged condition to 592.7 MPa to MPa after thermal aging and the fracture mode changed from ductile fracture into a ductile + quasi-cleavage fracture. The fusion zone (FZ) with the chemical composition gradient was about 40 µm from the Z2CND18.12N2 to ER308L. After thermal aging, spinodal decomposition and G-phase precipitation were observed for the first time in the ferrite phase of the FZ. Moreover, the hardness presented the following trend: FZ > ER308L > Z2CND18.12N2. The hardness of the ferrite phase dramatically increased from 6.13 GPa in an unaged condition to 8.46 GPa in a 10,000 h aged condition.