ABSTRACT
The mechanical behaviour of strain-hardening cement-based composites (SHCC) under monotonic tensile loading has been the subject of research for many years. The recent research on the SHCC's performance under cyclic loading has enabled the identification of a wide variety of damage phenomena different to those observed under monotonic loading. The article at hand first summarises the experimental evidence of such phenomena in the context of the material performance observed. On this basis, the mechanisms behind these phenomena are discussed and explained using rheological modelling.
ABSTRACT
Strain-hardening cement-based composites are a promising class of materials for a wide variety of applications due to their considerable tensile strength and pronounced ductility caused by the development of multiple fine cracks. Nevertheless, the safe use of such composites requires sound knowledge of their mechanical behaviour under different types of loading, particularly under fatigue loading, while considering distinct influences like initial crack width and fibre orientation. To deepen this knowledge, single-fibre pull-out tests on PVA-fibres from a cementitious matrix were carried out to gain information about the micro-mechanical and degradation processes of the fibre. It could be shown that the fibres tend to rupture instead of being pulled out under quasi-static loading. When changing the loading regime to alternating loading, this failure mechanism shifts to pull-out. By varying the experimental parameters such as initial crack width, inclination angle or compressive-force level a clear influence on the fibre's crack bridging capacity could be observed associated with effects on the degradation processes. Based on the data obtained, a micro-mechanical numerical model was developed to support the assumptions and observations from single-fibre pull-out tests and to enable predictions of the performance of the material on the microscale under cyclic loading.