Self-Discharge Processes in Symmetrical Supercapacitors with Activated Carbon Electrodes.

The self-discharge of an electric double-layer capacitor with composite activated carbon electrodes and aqueous electrolyte (1 M MgSO4) was studied in detail. Under a long-term potentiostatic charge (stabilization), a decrease in the discharge capacity was observed in the region of voltages exceeding 0.8 V. The self-discharge process consists of two phases. In the initial phase, the cell voltage drop is due to the charge redistribution inside electrodes. During the main phase, the charge transfer between the electrodes determines the voltage drop. The optimal stabilization time of the self-discharge was found to be 50 min at 1.4 V. Hydrophilization of the negative electrode occurred during long-term polarization due to the formation of epoxy functional groups.

Electrochemical Improvement of the MWCNT/Al Electrodes for Supercapacitors.

An original technique of chemical deposition (CVD) by catalytic pyrolysis of ethanol vapor was used to directly grow multiwall carbon nanotubes (MWCNTs) layers on aluminum foil. The grown nanotubes had excellent adhesion and direct electrical contact to the aluminum substrate. This material was perfect for use in electrochemical supercapacitors. In this work, the possibility of a significant increase in the specific capacity of MWCNTs by simple electrochemical oxidation was investigated. The optimal conditions for improving the characteristics of the MWCNT/Al electrodes were found. Electrochemical treatment of MWCNT/Al electrodes in a 0.005 M Na2SO4 solution at a potential of 4-5 V for 20-30 min increased the specific capacity of MWCNTs from 30 F/g to 140 F/g. The properties of modified nanotubes were investigated by X-ray photoelectron spectroscopy, cyclic voltammetry (CV), and impedance spectroscopy. A significant increase in the concentration of oxygen-containing functional groups on the surface of MWCNTs was found as a result of electrochemical oxidation. The modified MWCNT/Al electrodes maintained excellent stability to multiple charge-discharge cycles. After 20,000 CVs, the capacity loss was less than 5%. Thus, the results obtained significantly expanded the possibilities of using MWCNT/Al composite materials obtained by the method of direct deposition of carbon nanotubes on aluminum foil as electrodes for supercapacitors.

Reduced Graphene Oxide Aerogel inside Melamine Sponge as an Electrocatalyst for the Oxygen Reduction Reaction.

A graphene oxide aerogel (GOA) was formed inside a melamine sponge (MS) framework. After reduction with hydrazine at 60 °C, the electrical conductive nitrogen-enriched rGOA-MS composite material with a specific density of 20.1 mg/cm3 was used to fabricate an electrode, which proved to be a promising electrocatalyst for the oxygen reduction reaction. The rGOA-MS composite material was characterized by elemental analysis, scanning electron microscopy, X-ray photoelectron spectroscopy, and Raman spectroscopy. It was found that nitrogen in the material is presented by different types with the maximum concentration of pyrrole-like nitrogen. By using Raman scattering it was established that the rGOA component of the material is graphene-like carbon with an average size of the sp2-domains of 5.7 nm. This explains a quite high conductivity of the composite obtained.