ABSTRACT
Bamboo cellulose fiber (BF)-reinforced epoxy (EP) composites were fabricated with BF subjected to plasma treatment using argon (Ar), oxygen (O2), and nitrogen (N2) gases. Optimal mechanical properties of the EP/BF composites were achieved with BFs subjected to 30 min of plasma treatment using Ar. This is because Ar gas improved the plasma electron density, surface polarity, and BF roughness. Flexural strength and flexural modulus increased with O2 plasma treatment. Scanning electron microscopy images showed that the etching of the fiber surface with Ar gas improved interfacial adhesion. The water contact angle and surface tension of the EP/BF composite improved after 10 min of Ar treatment, owing to the compatibility between the BFs and the EP matrix. The Fourier transform infrared spectroscopy results confirmed a reduction in lignin after treatment and the formation of new peaks at 1736 cm-1, which indicated a reaction between epoxy groups of the EP and carbon in the BF backbone. This reaction improved the compatibility, mechanical properties, and water resistance of the composites.
ABSTRACT
The effect of argon (Ar) and oxygen (O2) gases as well as the treatment times on the properties of modified bamboo fibers using dielectric barrier discharge (DBD) plasma at generated power of 180 W were investigated. The plasma treatment of bamboo fibers with inert gases leads to the generation of ions and radicals on the fiber surface. Fourier transform-infrared spectroscopy (FTIR) confirmed that the functional groups of lignin and hemicellulose were reduced owing to the removal of the amorphous portion of the fibers by plasma etching. X-ray diffraction analysis (XRD) results in an increased crystallinity percentage. X-ray photoelectron spectroscopy (XPS) results showed the oxygen/carbon (O/C) atomic concentration ratio increased with increasing treatment time. The fiber weight loss percentage increased with increased treatment time. Scanning electron microscopy (SEM) images showed that partial etching of the fiber surface led to a higher surface roughness and area and that the Ar + O2 gas plasma treatment provided more surface etching than the Ar gas treatment because of the oxidation reaction of the O2 plasma. The mechanical properties of fiber-reinforced epoxy (FRE) matrix composites revealed that the F(tr)RE-Ar (30) samples showed a high tensile strength, whereas the mechanical properties of the F(tr)RE-Ar + O2 sample decreased with increased treatment time.