Preparation of organic/inorganic hybrid and hollow particles by catalytic deposition of silica onto core/shell heterocoagulates modified with poly[2-(N,N-dimethylamino)ethyl methacrylate].

The organic/inorganic hybrid particles PSt/P(St-CPEM)(θ)-g-PDMAEMA/SiO(2) were prepared by catalytic hydrolysis and subsequent polycondensation of tetraethoxysilane in the poly[2-(N,N-dimethylamino)ethyl methacrylate] (PDMAEMA) layers grafted on the PSt/P(St-CPEM)(θ) core/shell heterocoagulates. The micron-sized PSt core and the submicron-sized P(St-CPEM) shell particles bearing ATRP initiating groups were synthesized by dispersion polymerization of styrene (St) and emulsifier-free emulsion polymerization of St with 2-chloropropionyloxyethyl methacrylate (CPEM), respectively. The raspberry-shaped PSt/P(St-CPEM)(θ) heterocoagulates with a controlled surface coverage (θ=0.51, 0.81) were prepared by hydrophobic coagulation between the core and the shell particles in an aqueous NaCl solution near the T(g) of P(St-CPEM). Surface modification of heterocoagulates was carried out by ATRP of DMAEMA from the shell particles adsorbed on the core particles. Silica deposition was performed by simply adding tetraethoxysilane to a water/methanol dispersion of PSt/P(St-CPEM)(θ)-g-PDMAEMA. The SEM and TGA revealed that the resulting PSt/P(St-CPEM)(θ)-g-PDMAEMA/SiO(2) composites maintain a raspberry-like morphology after deposition of silica onto the PDMAEMA layer grafted on heterocoagulates. The micron-sized, raspberry-shaped or the submicron-sized, hole-structured silica hollow particles were obtained selectively by thermal decomposition of the PSt/P(St-CPEM)(θ)-g-PDMAEMA/SiO(2). The oriented particle array was fabricated by dropping anisotropically perforated silica particles onto a glass substrate settled at the bottom of a bottle filled with chloroform.