ABSTRACT
This study examined the impact of temperature optimization on indium tin oxide (ITO) films in monolithic HJT/perovskite tandem solar cells. ITO films were deposited using magnetron sputtering at temperatures ranging from room temperature (25 °C) to 250 °C. The sputtering target was ITO, with a mass ratio of In2O3 to SnO2 of 90% to 10%. The effects of temperature on the ITO film were analyzed using X-ray diffraction (XRD), spectroscopic ellipsometry, and sheet resistance measurements. Results showed that all ITO films exhibited a polycrystalline morphology, with diffraction peaks corresponding to planes (211), (222), (400), (440), and (622), indicating a cubic bixbyite crystal structure. The light transmittance exceeded 80%, and the sheet resistance was 75.1 Ω/sq for ITO deposited at 200 °C. The optical bandgap of deposited ITO films ranged between 3.90 eV and 3.93 eV. Structural and morphological characterization of the perovskite solar cell was performed using XRD and FE-SEM. Tandem solar cell performance was evaluated by analyzing current density-voltage characteristics under simulated sunlight. By optimizing the ITO deposition temperature, the tandem cell achieved a power conversion efficiency (PCE) of 16.74%, resulting in enhanced tandem cell efficiency.
ABSTRACT
BACKGROUND: The extent of the association between vitamin D deficiency and knee osteoarthritis remains inadequately understood. OBJECTIVE: This study aimed to elucidate the relationship between vitamin D levels and knee osteoarthritis through a cross-sectional analysis. METHODS: This retrospective study involved an analysis of knee radiographs and serum 25-hydroxyvitamin D3 (25-(OH) vitamin D3) levels in a cohort of 3424 individuals (2901 women and 523 men). Knee osteoarthritis severity was evaluated using the Kellgren-Lawrence radiological scoring system. RESULTS: Of the participants, 49.2% (n= 1,683) were diagnosed with knee osteoarthritis. Among these patients, the levels of adjusted 25-(OH) vitamin D3 were significantly lower (p< 0.001). Regression analysis revealed a significant association between vitamin D deficiency and knee osteoarthritis, with an adjusted odds ratio (OR) of 1.7 (95% CI: 1.5-2.0; p< 0.001). Notably, a stronger association was observed between vitamin D deficiency and knee osteoarthritis in women under 65 compared to those aged 65 and above. CONCLUSIONS: The findings of this study indicate a higher prevalence of vitamin D deficiency in patients with knee osteoarthritis. Maintaining adequate serum 25-(OH) vitamin D3 levels may prevent knee osteoarthritis, especially in women below 65.