Structure-Property Relationship of Polyetherimide Fibers Filled with Carbon Nanoparticles.

Nanocomposite fibers based on heat-resistant amorphous polyetherimide (PEI) were prepared by twin screw melt micro-extrusion. Vapor-grown carbon nanofibers (VGCFs) and single-wall carbon nanotubes (SWCNTs) were used as fillers which helped to achieve enhanced mechanical properties. The structure and mechanical properties of such nanocomposite fibers were studied. Electron microscopy and melt rheology data revealed a uniform distribution of the nanofillers throughout the volume of the fibers. Wide-angle X-ray scattering showed that the orientational drawing of the nanocomposite fibers led to an improved orientation of the filler particles along the fiber axis. VGCFs or SWCNTs increased the tensile strength and modulus (by ∼275 MPa and ∼5 GPa, respectively) in oriented nanocomposite fibers and decreased deformation at break. SWCNTs were found to be more effective reinforcers than VGCFs.

Effect of chitin nanofibrils on electrospinning of chitosan-based composite nanofibers.

Electrical conductivity, surface tension and viscosity of chitosan-based composite nanofibers are reported. 20 wt.% of chitin nanofibrils introduced into a chitosan solution leads to increase in viscosity of the mixture; the effect of shear rate becomes more pronounced. This phenomenon is caused by the formation of cluster structures involving filler particles, and by orientation of chitin nanofibrils under the action of shear stresses in electromagnetic field. Presence of chitin facilitated formation of nanofibers in electric field and led to significant decrease in the amount of defects.

3D superstructures with an orthorhombic lattice assembled by colloidal PbS quantum dots.

We report a new type of metamaterial comprising a highly ordered 3D network of 3-7 nm lead sulfide quantum dots self-assembled in an organic matrix formed by amphiphilic ligands (oleic acid molecules). The obtained 3D superstructures possess an orthorhombic lattice with the distance between the nanocrystals as large as 10-40 nm. Analysis of self-assembly and destruction of the superstructures in time performed by a SAXS technique shows that their morphology depends on the quantity of amphiphilic ligands and width of the quantum dot size and its distribution. Formation of the superstructures is discussed in terms of a model describing the lyotropic crystal formation by micelles from three-phase mixtures. The results show that the organic molecules possessing surfactant properties and capable of forming micelles with nanoparticles as a micelle core can be utilized as building blocks for the creation of novel metamaterials based on a highly ordered 3D network of semiconductors, metals or magnetic nanoparticles.

Wet spinning of fibers made of chitosan and chitin nanofibrils.

Biocompatible and bioresorbable composite fibers consisting of chitosan filled with anisotropic chitin nanofibrils with the length of 600-800 nm and cross section of about 11-12 nm as revealed by SEM and XRD were prepared by coagulation. Both chitin and chitosan components of the composite fibers displayed preferred orientations. Orientation of chitosan molecules induced by chitin nanocrystallites was confirmed by molecular modeling. The incorporation of 0.1-0.3 wt.% of chitin nanofibrils into chitosan matrix led to an increase in strength and Young modulus of the composite fibers.