ABSTRACT
The aim of this work is to synthesize and characterize a nanostructured material with improved parameters suitable as a chemiresistive gas sensor sensitive to propylene glycol vapor (PGV). Thus, we demonstrate a simple and cost-effective technology to grow vertically aligned carbon nanotubes (CNTs) and fabricate a PGV sensor based on Fe2O3:ZnO/CNT material using the radio frequency magnetron sputtering method. The presence of vertically aligned carbon nanotubes on the Si(100) substrate was confirmed by scanning electron microscopy and Fourier transform infrared (FTIR), Raman, and energy-dispersive X-ray spectroscopies. The uniform distribution of elements in both CNTs and Fe2O3:ZnO materials was revealed by e-mapped images. The hexagonal shape of the ZnO material in the Fe2O3:ZnO structure and the interplanar spacing in the crystals were clearly visible by transmission electron microscopy images. The gas-sensing behavior of the Fe2O3:ZnO/CNT sensor toward PGV was investigated in the temperature range of 25-300 °C with and without ultraviolet (UV) irradiation. The sensor showed clear and repeatable response/recovery characteristics in the PGV range of 1.5-140 ppm, sufficient linearity of response/concentration dependence, and high selectivity both at 200 and 250 °C without UV radiation. This is a basis for concluding that the synthesized Fe2O3:ZnO/CNT structure is the best candidate for use in PGV sensors, which will allow its further successful application in real-life sensor systems.
ABSTRACT
In this report, a Fe2O3:ZnO sputtering target and a nanograins-based sensor were developed for the room temperature (RT) detection of hydrogen peroxide vapor (HPV) using the solid-state reaction method and the radio frequency (RF) magnetron sputtering technique, respectively. The characterization of the synthesized sputtering target and the obtained nanostructured film was carried out by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and energy-dispersive X-ray (EDX) analyses. The SEM and TEM images of the film revealed its homogeneous granular structure, with a grain size of 10-30 nm and an interplanar spacing of Fe2O3 and ZnO, respectively. EDX spectroscopy presented the real concentrations of Zn in the target material and in the film (21.2 wt.% and 19.4 wt.%, respectively), with a uniform distribution of O, Al, Zn, and Fe elements in the e-mapped images of the Fe2O3:ZnO film. The gas sensing behavior was investigated in the temperature range of 25-250 °C with regards to the 1.5-56 ppm HPV concentrations, with and without ultraviolet (UV) irradiation. The presence of UV light on the Fe2O3:ZnO surface at RT reduced a low detection limit from 3 ppm to 1.5 ppm, which corresponded to a response value of 12, with the sensor's response and recovery times of 91 s and 482 s, respectively. The obtained promising results are attributed to the improved characteristics of the Fe2O3:ZnO composite material, which will enable its use in multifunctional sensor systems and medical diagnostic devices.
ABSTRACT
Melamine sponges were coated with polypyrrole during the in situ polymerization of pyrrole. The precipitation polymerization was compared with the dispersion mode, that is, with the preparation in the presence of poly(N-vinylpyrrolidone) and nanosilica as colloidal stabilizers. The coating of sponges during the dispersion polymerization leads to the elimination of the undesired polypyrrole precipitate, improved conductivity, and increased specific surface area. The sponges were tested with respect to their conductivity and as pressure-sensitive conducting materials with antibacterial performance.
ABSTRACT
Polypyrrole one-dimensional nanostructures (nanotubes, nanobelts and nanofibers) were prepared using three various dyes (Methyl Orange, Methylene Blue and Eriochrome Black T). Their high electrical conductivity (from 17.1 to 60.9 S cm-1), good thermal stability (in the range from 25 to 150 °C) and resistivity against ageing (half-time of electrical conductivity around 80 days and better) were used in preparation of lightweight and flexible composites with silicone for electromagnetic interference shielding in the C-band region (5.85-8.2 GHz). The nanostructures' morphology and chemical structure were characterized by scanning electron microscopy, Brunauer-Emmett-Teller specific surface measurement and attenuated total reflection Fourier-transform infrared spectroscopy. DC electrical conductivity was measured using the Van der Pauw method. Complex permittivity and AC electrical conductivity of respective silicone composites were calculated from the measured scattering parameters. The relationships between structure, electrical properties and shielding efficiency were studied. It was found that 2 mm-thick silicone composites of polypyrrole nanotubes and nanobelts shield almost 80% of incident radiation in the C-band at very low loading of conductive filler in the silicone (5% w/w). Resulting lightweight and flexible polypyrrole composites exhibit promising properties for shielding of electromagnetic interference in sensitive biological and electronic systems.