ABSTRACT
Photoelectrochemical (PEC) devices that use semiconductors to absorb solar light for water splitting offer a promising way toward the future scalable production of renewable hydrogen fuels. However, the charge recombination in the photoanode/electrolyte (solid/liquid) junction is a major energy loss and hampers the PEC performance from being efficient. Here, we show that this problem is addressed by the conformal deposition of an ultrathin p-type NiO layer on the photoanode to create a buried p/n junction as well as to reduce the charge recombination at the surface trapping states for the enlarged surface band bending. Further, the in situ formed hydroxyl-rich and hydroxyl-ion-permeable NiOOH enables the dual catalysts of CoO(x) and NiOOH for the improved water oxidation activity. Compared to the CoO(x) loaded BiVO4 (CoO(x)/BiVO4) photoanode, the â¼6 nm NiO deposited NiO/CoO(x)/BiVO4 photoanode triples the photocurrent density at 0.6 V(RHE) under AM 1.5G illumination and enables a 1.5% half-cell solar-to-hydrogen efficiency. Stoichiometric oxygen and hydrogen are generated with Faraday efficiency of unity over 12 h. This strategy could be applied to other narrow band gap semiconducting photoanodes toward the low-cost solar fuel generation devices.
ABSTRACT
BaNbO2 N is a semiconductor photocatalyst active for water oxidation under visible-light irradiation up to λ=740 nm. It is important to understand the nitridation processes of precursor materials to form BaNbO2 N to tune the physical properties and improve the photocatalytic activity. Comprehensive experiments and analyses of temperatures, durations, ammonia flow rates, and barium/niobium ratios in the precursor during the nitridation process reveals that faster ammonia flow rates and higher barium/niobium ratios in the precursors help to suppress reduction of pentavalent niobium ions in the nitridation products and that the use of a precursor prepared by a soft-chemistry route allows the production of BaNbO2 N at lower temperatures in shorter times than the use of physical mixtures of BaCO3 and Nb2 O5 because the niobium species is dispersed among the barium species. BaNbO2 N prepared by the soft-chemistry route exhibits comparatively higher activity than that prepared from physical mixtures of BaCO3 and Nb2 O5 , probably because of lower nitridation temperatures, which suppress excessive dissociation of ammonia, and thereby reduce pentavalent niobium ions, and intimate interaction of niobium and barium sources, which lowers the densities of mid-gap states associated with defects.