Abrasive Sensitivity of Martensitic and a Multi-Phase Steels under Different Abrasive Conditions.

The wear behaviour of two martensitic and one multiphase steel targeted for abrasion and erosion applications in agriculture and mining industry were investigated in three abrasive test systems with different complexity. Scratch tests were performed with different indenter radii, shapes, and loads. The material behaviour was also investigated in multi-asperity contact systems. Pin-on-disc tests were performed with various loads and abrasive particles, as well as abrasive slurry-pot tests with different sliding velocities, distances, and impact angles of the abrasive media were performed. Comparing the test systems, the tested materials ranked similarly based on their wear performance, however, in each configuration, the dominant variable of the wear mechanism differed. The significance and contributions of test paramecenterters, the material's mechanical properties (H, σM, σY, E, εεM, εεB, W, σc, Ec) and the dimensionless numbers formed from them were investigated on the wear behaviour and the surface deformation. Correlation between parameters was established by multiple linear regression models. The sensitivity of the tested materials to abrasion was evaluated taking into account the wide range of influencing parameters.

The Effect of Crystallinity on the Toughness of Cast Polyamide 6 Rods with Different Diameters.

The present paper concentrates on the toughness and the degree of crystallinity of the magnesium-catalyzed polyamide 6 rods cast in different diametres, which are commonly used for gear manufacturing. Its toughness cannot be regarded as a constant feature due to the casting technology. The mechanical properties of the semi-finished products are sensitive to the manufactured dimension, e.g., cast diameter, which are investigated by the Charpy impact test and tensile impact test. It is generally accepted that the impact strength and tensile-impact strength correlate with the degree of crystallinity beside many other material's feature. Crystallinity is evaluated by Differential Scanning Calorimetry. The aim of this study is to determine the relationship between toughness and crystallinity of the magnesium-catalyzed cast PA6 rods with different diameters. For the research cast rods between 40 and 300 mm diameter were selected in seven-dimensional steps. Based on the results, it was found that the toughness depends strongly on the diameter size. Furthermore, it is proved that the crystallinity explains 62.3% of the variation of the Charpy's impact strengths, while the tensile impact method was not suitable to detect the difference between the test samples.