Bubble Attachment to Cellulose and Silica Surfaces of Varied Surface Energies: Wetting Transition and Implications in Foam Forming.

To better understand the complex system of wet foams in the presence of cellulosic fibers, we investigate bubble-surface interactions by following the effects of surface hydrophobicity and surface tension on the contact angle of captive bubbles. Bubbles are brought into contact with model silica and cellulose surfaces immersed in solutions of a foaming surfactant (sodium dodecyl sulfate) of different concentrations. It is observed that bubble attachment is controlled by surface wetting, but a significant scatter in the behavior occurs near the transition from partial to complete wetting. For chemically homogeneous silica surfaces, this transition during bubble attachment is described by the balance between the energy changes of the immersed surface and the frictional surface tension of the moving three-phase contact line. The situation is more complex with chemically heterogeneous, hydrophobic trimethylsilyl cellulose (TMSC). TMSC regeneration, which yields hydrophilic cellulose, causes a dramatic drop in the bubble contact angle. Moreover, a high interfacial tension is required to overcome the friction caused by microscopic (hydrophilic) pinning sites of the three-phase contact line during bubble attachment. A simple theoretical framework is introduced to explain our experimental observations.

Cellulose nanofibrils prepared by gentle drying methods reveal the limits of helium ion microscopy imaging.

TEMPO-oxidized cellulose nanofibrils (TCNFs) have unique properties, which can be utilised in many application fields from printed electronics to packaging. Visual characterisation of TCNFs has been commonly performed using Scanning Electron Microscopy (SEM). However, a novel imaging technique, Helium Ion Microscopy (HIM), offers benefits over SEM, including higher resolution and the possibility of imaging non-conductive samples uncoated. HIM has not been widely utilized so far, and in this study the capability of HIM for imaging of TCNFs was evaluated. Freeze drying and critical point drying (CPD) techniques were applied to preserve the open fibril structure of the gel-like TCNFs. Both drying methods worked well, but CPD performed better resulting in the specific surface area of 386 m2 g-1 when compared to 172 m2 g-1 and 42 m2 g-1 of freeze dried samples frozen in propane and nitrogen, respectively. HIM imaging of TCNFs was successful but high magnification imaging was challenging because the ion beam tended to degrade the TCNFs. The effect of the imaging parameters on the degradation was studied and an ion dose as low as 0.9 ion per nm2 was required to prevent the damage. This study points out the differences between the gentle drying methods of TCNFs and demonstrates beam damage during imaging like none previously reported with HIM. The results can be utilized in future studies of cellulose or other biological materials as there is a growing interest for both the HIM technique and bio-based materials.