ABSTRACT
The characteristics of a novel 0D/3D heterojunction photodetector fabricated using solution-processed colloidal MoS2 quantum dots (QDs) on GaAs is presented. MoS2 QDs with a dimension of â¼2 nm, synthesized by a standard sono-chemical exfoliation process with 2D layers have been used for the purpose. The microscopic and spectroscopic studies confirmed the formation of semiconducting (2H phase) MoS2 QDs. The photodetectors were fabricated using n-GaAs substrates with two different doping concentrations resulting in n-n heterojunctions between n-type 0D MoS2 QDs and bulk n-GaAs. The devices fabricated using GaAs with a higher doping concentration, showed an increase in the reverse current of the order of â¼102 upon illumination, while the same with a lower doping concentration showed an increase of the order of â¼103. All the heterojunction photodetector devices show a broadband operation over the visible wavelength range of 400-950 nm, with a peak responsivity of the devices being observed at 500 nm. The peak responsivity and detectivity are found to be â¼400 mA W-1 and â¼4 × 1012 Jones, respectively, even without any external applied bias, which are useful for self-powered photodetection. The results indicate that colloidal MoS2/GaAs based hybrid heterostructures provide a platform for fabricating broadband photodetectors by using highly absorbing MoS2 QDs, which may show the pathway towards next-generation optoelectronic devices with superior detection properties.