ABSTRACT
Electron beam additive wire-feed manufacturing of Cu-3wt.%S-0.8wt.%Mn bronze thin wall on a stainless steel substrate has been carried out at heat input levels of 0.19, 0.25, and 0.31 kJ/mm. The microstructures of as-deposited metal ranged from low aspect ratio columnar with equiaxed grain layers to zig-zagged and high aspect ratio columnar, as depended on the heat input. Post-deposition annealing at 900 °C for 6 h resulted in recrystallization of the high aspect ratio columnar grains with further grain growth by boundary migration. Pre-deformation by 10% thickness reduction and then annealing at 900 °C for 6 h also allowed obtaining recrystallized grain structures with less fraction of twin boundaries but higher fraction of high-angle ones, as compared to those of only annealed sample. Pre-deformation and ensuing annealing allowed simultaneous increasing of the ultimate tensile strength and strain-to-fracture.
ABSTRACT
Electron beam additive wire-feed deposition of Cu-7.5wt.%Al bronze on a stainless-steel substrate has been carried out at heat input levels 0.21, 0.255, and 0.3 kJ/mm. The microstructures formed at 0.21 kJ/mm were characterized by the presence of both zigzagged columnar and small equiaxed grains with 10% of Σ3 annealing twin grain boundaries. No equiaxed grains were found in samples obtained at 0.255 and 0.3 kJ/mm. The zigzagged columnar ones were only retained in samples obtained at 0.255 kJ/mm. The fraction of Σ3 boundaries reduced at higher heat input values to 7 and 4%, respectively. The maximum tensile strength was achieved on samples obtained with 0.21 kJ/mm as tested with a tensile axis perpendicular to the deposited wall's height. More than 100% elongation-to-fracture was achieved when testing the samples obtained at 0.3 kJ/mm (as tested with a tensile axis coinciding with the wall's height).