ABSTRACT
CdS films with a wide range of substrate temperatures as deposition parameters were fabricated on Corning Eagle 2000 glass substrates using RF magnetron sputtering. The crystallographic structure, microscopic surface texture, and stoichiometric and optical properties of each CdS film deposited at various substrate temperatures were observed to be highly temperature-dependent. The grown CdS thin films revealed a polycrystalline structure in which a cubic phase was mixed based on a hexagonal wurtzite phase. The relative intensity of the H(002)/C(111) peak, which represents the direction of the preferential growth plane, enhanced as the temperatures climbed from 25 °C to 350 °C. On the contrary, the intensity of the main growth peak at the higher temperatures of 450 °C and 500 °C was significantly reduced and exhibited amorphous-like behavior. The sharp absorption edge revealed in the transmission spectrum shifted from the long wavelength to the short wavelength region with the rise in the substrate temperature. The bandgap showed a tendency to widen from 2.38 eV to 2.97 eV when the temperatures increased from 25 °C to 350 °C. The CdS films grown at the temperatures of 450 °C and 500 °C exhibited glass-like transmittance with almost no interference fringes of light, which resulted in wide bandgap values of 3.09 eV and 4.19 eV, respectively.
ABSTRACT
Hexagonal boron nitride was synthesized by pyrolysis using boric acid and melamine. At this time, to impart luminescence, rare earth cerium ions were added to synthesize hexagonal boron nitride nanophosphor particles exhibiting deep blue emission. To investigate the changes in crystallinity and luminescence according to the re-heating temperature, samples which had been subjected to pyrolysis at 900 °C were subjected to re-heating from 1100 °C to 1400 °C. Crystallinity and luminescence were enhanced according to changes in the reheating temperature. The synthesized cerium ion-doped hexagonal boron nitride nanoparticle phosphor was applied to the anti-counterfeiting field to prepare an ink that can only be identified under UV light.
ABSTRACT
Barium tungstate (BaWO4) powders with various sintering temperatures, and BaWO4:Dy3+ phosphor samples with concentrations of different rare-earth (RE) activator ions (Dy3+, Sm3+, Tb3+) were prepared through co-precipitation. The structural, morphological, and photoluminescent characteristics of barium tungstate phosphors depend on the concentration of RE ions. The crystallographic characteristics of the synthesized BaWO4 were analyzed using X-ray diffraction (XRD) patterns. The size and shape of the crystalline particles were estimated based on images measured with a field emission scanning electron microscope (FE-SEM). As the sintering temperature of the BaWO4 particles increased from 400 °C to 1000 °C, the size of the particles gradually increased and showed a tendency to clump together. In the sample doped with 7 mol % Dy3+ ions, the intensity of all emission bands reached their maximum. The emission spectra of the RE3+-doped BaWO4 powders by excitation at 325 nm were composed of yellow (Dy3+), red (Sm3+), and green (Tb3+) band at 572, 640, and 544 nm. This indicates that most of the RE3+ ions absorbed the position without reversal symmetry in the BaWO4 lattice. These results propose that strong emission intensity and tunable color for the phosphors can be accomplished by rare-earth doped host with an suitable quantity. In addition, the phosphor thin films, having high transparency from aqueous colloidal solutions, were deposited on banknotes, and it is considered whether it is suitable for anti-counterfeiting applications.