ABSTRACT
Eco-friendly flame retardants are greatly required to meet the expectations of low-toxicity, environmental compatibility and sustainability. Extracellular polymeric substances (EPS), the biopolymers recovered from excess granular wastewater sludge, have been successfully incorporated into poly(vinyl alcohol) (PVA) by a solution casting method. Self-extinguishment of EPS was observed in a vertical burn test. Positive effects of EPS on the reduction of heat release rate and CO emission of EPS/PVA composites were also demonstrated. The presence of various types of phosphates was detected in the EPS and a possible flame-retardant mechanism has been proposed. The investigation of using granular sludge EPS to reduce the flammability of synthetic polymers may open the possibility of converting wastewater sludge into bio phosphorus-based flame retardants.
Subject(s)
Sewage , Wastewater , Biopolymers , Extracellular Polymeric Substance Matrix , Polymers , Waste Disposal, FluidABSTRACT
The flame-retardant performance of materials has become an increasingly crucial factor for society across a broad range of applications in aircraft, automobiles, civil infrastructure, and consumer products [...].
ABSTRACT
In this work, the fire reaction properties of flax-polypropylene (PP) composites were investigated at multiple sample angles both experimentally and numerically under two different heat flux conditions (35 and 50 kW/m2) in the cone calorimeter environment. An innovative testing setup which can accommodate a wide range of angles between 0° and 90° for the sample angle frame was developed to perform cone calorimeter tests at different sample angles. An advanced numerical predictive model based on the finite volume method was developed using the fire dynamics simulator (FDS) to quantify the dependency of ignition and combustion properties with sample angles. The numerical model was validated against experimental data from the cone calorimeter tests. The experimental and numerical analyses were conducted to quantify the effects of sample orientation on the different fire reaction properties i.e., ignition time, ignition temperature, burn time, heat release rate (HRR), critical heat flux, etc. The numerical method was utilised to analyse the mechanisms controlling the effect of heat convection and radiation blockage on the heating process. The study establishes that the sample orientation (with respect to the heat flux normal) has a significant influence on the fire reaction properties of natural fibre composites.
ABSTRACT
The integration of intumescent flame-retardant (IFR) additives in natural fiber-based polymer composites enhances the fire-retardant properties, but it generally has a detrimental effect on the mechanical properties, such as tensile and flexural strengths. In this work, the feasibility of graphene as a reinforcement additive and as an effective synergist for IFR-based flax-polypropylene (PP) composites was investigated. Noticeable improvements in tensile and flexural properties were achieved with the addition of graphene nanoplatelets (GNP) in the composites. Furthermore, better char-forming ability of GNP in combination with IFR was observed, suppressing HRR curves and thus, lowering the total heat release (THR). Thermogravimetric analysis (TGA) detected a reduction in the decomposition rate due to strong interfacial bonding between GNP and PP, whereas the maximum decomposition rate was observed to occur at a higher temperature. The saturation point for the IFR additive along with GNP has also been highlighted in this study. A safe and effective method of graphene encapsulation within PP using the fume-hood set-up was achieved. Finally, the effect of flame retardant on the flax-PP composite has been simulated using Fire Dynamics Simulator.
ABSTRACT
Even though casein has an intrinsic potential ability to act as a flame retardant (FR) additive, the research regarding the FR performance of casein filled polymeric composites has not been thoroughly conducted. In the present work, two commercial casein products, such as lactic casein 720 (LAC) and sodium casein 180 (SC), were chosen to investigate their effects on the performances of the polypropylene (PP) composites. The melt compounding and compression moulding processes were employed to fabricate these casein-based composites. Ammonium polyphosphate (APP) was also selected to explore its combined effects in conjunction with casein on the composite's flammability. The cone calorimeter results showed that the addition of casein significantly reduced (66%) the peak heat release rate (PHRR) of the composite compared to that of neat PP. In particular, the combination of LAC and APP led to the formation of more compact and rigid char compared to that for SC based sample; hence, a further reduction (80%) in PHRR and self-extinguishment under a vertical burn test were accomplished. Moreover, the tensile modulus of the composite improved (23%) by the combined effects of LAC and APP. The overall research outcome has established the potential of casein as a natural protein FR reducing a polymer's flammability.
ABSTRACT
Carbon based fillers have attracted a great deal of interest in polymer composites because of their ability to beneficially alter properties at low filler concentration, good interfacial bonding with polymer, availability in different forms, etc. The property alteration of polymer composites makes them versatile for applications in various fields, such as constructions, microelectronics, biomedical, and so on. Devastations due to building fire stress the importance of flame-retardant polymer composites, since they are directly related to human life conservation and safety. Thus, in this review, the significance of carbon-based flame-retardants for polymers is introduced. The effects of a wide variety of carbon-based material addition (such as fullerene, CNTs, graphene, graphite, and so on) on reaction-to-fire of the polymer composites are reviewed and the focus is dedicated to biochar-based reinforcements for use in flame retardant polymer composites. Additionally, the most widely used flammability measuring techniques for polymeric composites are presented. Finally, the key factors and different methods that are used for property enhancement are concluded and the scope for future work is discussed.
ABSTRACT
In this research, extracellular polymeric substances (EPS), such as EPSflocs and EPSgranules, were successfully extracted from activated and aerobic granular sludge, respectively, and tested as bio-based flame retardant materials. Flax fabric was coated by the biopolymeric substances and its flammability was evaluated based on a vertical burning test defined in US Federal Aviation Regulation. Both EPSflocs and EPSgranules coated flax fabrics achieved the self-extinguishment due to effective char formation. In particular, the result of the EPSgranules coated sample met the aviation requirements for the aircraft interior. Moreover, the presence of carbonated hydroxyapatite was identified in EPSgranules char residue by using FTIR and XRD analysis. It can contribute to the self-extinguishing property of the fabric by enhancing char formation. Thermogravimetric analysis also demonstrated that EPSgranules coated flax was able to produce greater amount of char residue and its decomposition rate was significantly reduced. This research indicates that there is a great potential to use this biopolymer as a resource for developing high performance bio-inspired flame retardant materials and contribute to a circular economy.
Subject(s)
Flame Retardants , Flax , Extracellular Polymeric Substance Matrix , Sewage , TextilesABSTRACT
Four biomass wastes (rice husk, coffee husk, coarse wool, and landfill wood) were added with biochar and polypropylene (PP) to manufacture biocomposites. Individual biomasses were tested for their combustion behavior using cone calorimeter. Biocomposites were analyzed for their fire/thermal, mechanical, and morphological properties. Wood had the most desirable comprehensive effect on both the mechanical and fire properties of composites. In particular, wood and biochar composite exhibited the highest values of tensile/flexural properties with a relatively low peak heat release rate. In general, application of waste derived biochar and biomasses drastically reduced the susceptibility of neat PP towards fire.