Blister-based-laser-induced-forward-transfer: a non-contact, dry laser-based transfer method for nanomaterials.

We show that blister-based-laser-induced forward-transfer can be used to cleanly desorb and transfer nano- and micro-scale particles between substrates without exposing the particles to the laser radiation or to any chemical treatment that could damage the intrinsic electronic and optical properties of the materials. The technique uses laser pulses to induce the rapid formation of a blister on a thin metal layer deposited on glass via ablation at the metal/glass interface. Femtosecond laser pulses are advantageous for forming beams of molecules or small nanoparticles with well-defined velocity and narrow angular distributions. Both fs and ns laser pulses can be used to cleanly transfer larger nanoparticles including relatively fragile monolayer 2D transition metal dichalcogenide crystals and for direct transfer of nanoparticles from chemical vapour deposition growth substrates, although the mechanisms for inducing blister formation are different.

Fabrication and characterization of fully flattened carbon nanotubes: a new graphene nanoribbon analogue.

Graphene nanoribbons (GNR) are one of the most promising candidates for the fabrication of graphene-based nanoelectronic devices such as high mobility field effect transistors (FET). Here, we report a high-yield fabrication of a high quality another type of GNR analogue, fully flattened carbon nanotubes (flattened CNTs), using solution-phase extraction of inner tubes from large-diameter multi-wall CNTs (MWCNTs). Transmission electron microscopy (TEM) observations show that flattened CNTs have width of typically 20 nm and a barbell-like cross section. Measurements of the low-bias conductance of isolated flattened CNTs as a function of gate voltage shows that the flattened CNTs display ambipolar conduction which is different from those of MWCNTs. The estimated gap based on temperature dependence of conductivity measurements of isolated flattened CNTs is 13.7 meV, which is probably caused by the modified electronic structure due to the flattening.

Purity-enhanced bulk synthesis of thin single-wall carbon nanotubes using iron-copper catalysts.

We report high purity and high yield synthesis of single-wall carbon nanotubes (SWCNTs) of narrow diameter from iron-copper bimetal catalysts. The SWCNTs with diameter of 0.8-1.2 nm are synthesized using the zeolite-supported alcohol chemical vapour deposition method. Single metal and bimetal catalysts are systematically investigated to achieve both the enhancement of SWCNT yield and the suppression of the undesired formation of graphitic impurities. The relative yield and purity of SWCNTs are quantified using optical absorption spectroscopy with an ultracentrifuge-based purification technique. For the single metal catalyst, iron shows the highest catalytic activity compared with the other metals such as cobalt, nickel, molybdenum, copper, and platinum. It has been found that the addition of copper to iron results in the suppression of carbonaceous impurity formation without decreasing the SWCNT yield. The purity-enhanced SWCNT shows fairly low sheet resistance due to the improvement of inter-nanotube contacts. This scalable design of SWCNT synthesis with enhanced purity is therefore a promising tool for shaping future high performance devices.