ABSTRACT
In order to acquire a flexible resistive heating element in the temperature range for human body heating, the influence of DC voltage on chloroprene rubber (CR) and carbon black (CB) composites has been investigated. Three conduction mechanisms have been found to occur in the range from 0.5 V to 10 V - charge velocity increase due to the increase of the electric field, matrix thermal expansion that results in decreased tunnelling currents and new electroconductive channel formation at voltages above 7.5 V, where the temperature exceeds the matrix's softening point. As opposed to external heating, during resistive heating, the composite exhibits a negative temperature coefficient of resistivity up to an applied voltage of 5 V. The intrinsic electro-chemical matrix properties play an important role in the overall resistivity of the composite. The material shows cyclical stability when repeatedly applying a voltage of 5 V and can be used as a human body heating element.
ABSTRACT
Polymer contact electrification offers the possibility to harvest mechanical energy using lightweight, flexible and low-cost materials, but the mechanism itself is still unresolved. Several recent studies confirm heterolytic covalent bond breaking as the mechanism for surface charge formation. Here it is shown that the reason for the formation of surface charge by contacting two identical polymers results from the fluctuation in the surface irregularities, and that contacted materials with a greater porosity or surface roughness differential result in a greater generation of surface charge. Porosity and surface roughness create uneven surface length percentage changes in the lateral direction during deformation, which changes the charge density across the surface during relaxation. Multilayered membranes exhibit flexoelectric properties upon pressing and releasing by generating charge without separating individual membrane layers. This new insight deepens the understanding of polymer contact electrification and highlights better ways to prepare triboelectric or flexoelectric nanogenerator devices.
ABSTRACT
By using a solvent-based method composites of ethylenevinyl acetate copolymer and carbon black (EVA-CB) were synthesized for sensing BTEX (benzene, toluene, ethylbenzene and xylene) vapours. The composites were characterized using atomic force microscopy (AFM) in an electroconductive mode. Gas sensing results show that EVA-CB can reproducibly detect BTEX and that the response increases linearly with vapour concentration. Compared to gas-sensing measurements of gasoline vapours, the responses with toluene and ethylbenzene are different and can be explained by varying side chains of the benzene ring.