Correlation Between Two-Dimensional Electron Gas Mobility and Crystal Quality in AlGaN/GaN High-Electron-Mobility Transistor Structure Grown on 4H-SiC.

We investigated the correlation between the crystal quality and two-dimensional electron gas (2DEG) mobility of an AlGaN/GaN high-electron-mobility transistor (HEMT) structure grown by metal-organic chemical vapor deposition. For the structure with an AlN nucleation layer grown at 1100 °C, the 2DEG mobility and sheet carrier density were 1627 cm²/V·s and 3.23 × 10¹³ cm⁻², respectively, at room temperature. Further, it was confirmed that the edge dislocation density of the GaN buffer layer was related to the 2DEG mobility and sheet carrier density in the AlGaN/GaN HEMT.

GaN Epitaxial Layer Grown with Conductive Al(x)Ga(1-x)N Buffer Layer on SiC Substrate Using Metal Organic Chemical Vapor Deposition.

This study investigated GaN epitaxial layer growth with a conductive Al(x)Ga(1-x)N buffer layer on n-type 4H-SiC by high-temperature metalorganic chemical vapor deposition (HT-MOCVD). The Al composition of the Al(x)Ga(1-x)N buffer was varied from 0% to 100%. In terms of the crystal quality of the GaN layer, 79% Al was the optimal composition of the Al(x)Ga(1-x)N buffer layer in our experiment. A vertical conductive structure was fabricated to measure the current voltage (I-V) characteristics as a function of Al composition, and the I-V curves showed that the resistance increased with increasing Al concentration of the Al(x)Ga(1-x)N buffer layer.