ABSTRACT
Virucidal filter materials were prepared by electrospinning a solution of 28 wt % poly(vinylidene difluoride) in N,N-dimethylacetamide without and with the addition of 0.25 wt %, 0.75 wt %, 2.0 wt %, or 3.5 wt % Cu(NO3)2 · 2.5H2O as virucidal agent. The fabricated materials had a uniform and defect free fibrous structure and even distribution of copper nanoclusters. X-ray diffraction analysis showed that during the electrospinning process, Cu(NO3)2 · 2.5H2O changed into Cu2(NO3)(OH)3. Electrospun filter materials obtained by electrospinning were essentially macroporous. Smaller pores of copper nanoclusters containing materials resulted in higher particle filtration than those without copper nanoclusters. Electrospun filter material fabricated with the addition of 2.0 wt % and 3.5 wt % of Cu(NO3)2 · 2.5H2O in a spinning solution showed significant virucidal activity, and there was 2.5 ± 0.35 and 3.2 ± 0.30 logarithmic reduction in the concentration of infectious SARS-CoV-2 within 12 h, respectively. The electrospun filter materials were stable as they retained virucidal activity for three months.
ABSTRACT
Highly microporous adsorbents have been under considerable scrutiny for efficient adsorptive storage of H2. Of specific interest are sustainable, chemically activated, microporous carbon adsorbents, especially from renewable and organic precursor materials. In this article, six peat-derived microporous carbon materials were synthesized by chemical activation with ZnCl2. N2 and CO2 gas adsorption data were measured and simultaneously fitted with the 2D-NLDFT-HS model. Thus, based on the obtained results, the use of a low ratio of ZnCl2 for chemical activation of peat-derived carbon yields highly ultramicroporous carbons which are able to adsorb up to 83% of the maximal adsorbed amount of adsorbed H2 already at 1 bar at 77 K. This is accompanied by the high ratio of micropores, 99%, even at high specific surface area of 1260 m2 g-1, exhibited by the peat-derived carbon activated at 973 K using a 1:2 ZnCl2 to peat mass ratio. These results show the potential of using low concentrations of ZnCl2 as an activating agent to synthesize highly ultramicroporous carbon materials with suitable pore characteristics for the efficient low-pressure adsorption of H2.
ABSTRACT
Herein we demonstrate how peat, abundant and cheap biomass, can be successfully used as a precursor to synthesize peat-derived hard carbons (PDCs), applicable as electrode materials for sodium-ion batteries (SIB). The PDCs were obtained by pre-pyrolysing peat at 300-800 °C, removing impurities with base-acid solution treatment and thereafter post-pyrolysing the materials at temperatures (T) from 1000 to 1500 °C. By modification of pre- and post-pyrolysis temperatures we obtained hard carbons with low surface areas, optimal carbonization degree and high electrochemical Na+ storage capacity in SIB half-cells. The best results were obtained when pre-pyrolysing peat at 450 °C, washing out the impurities with KOH and HCl solutions and then post-pyrolysing the obtained carbon-rich material at 1400 °C. All hard carbons were electrochemically characterized in half-cells (vs. Na/Na+) and capacities as high as 350 mA h g-1 at 1.5 V and 250 mA h g-1 in the plateau region (E < 0.2 V) were achieved at charging current density of 25 mA g-1 with an initial coulombic efficiency of 80%.