ABSTRACT
CuFeS2/TiO2 nanocomposite has been prepared by a simple, low-cost mechanochemical route to assess its visible-light-driven photocatalytic efficiency in Methyl Orange azo dye decolorization. The structural and microstructural characterization was studied using X-ray diffraction and high-resolution transmission electron microscopy. The presence of both components in the composite and a partial anatase-to-rutile phase transformation was proven by X-ray diffraction. Both components exhibit crystallite size below 10 nm. The crystallite size of both phases in the range of 10-20 nm was found and confirmed by TEM. Surface and morphological properties were characterized by scanning electron microscopy and nitrogen adsorption measurement. Scanning electron microscopy has shown that the nanoparticles are agglomerated into larger grains. The specific surface area of the nanocomposite was determined to be 21.2 m2·g-1. Optical properties using UV-Vis and photoluminescence spectroscopy were also investigated. CuFeS2/TiO2 nanocomposite exhibits strong absorption with the determined optical band gap 2.75 eV. Electron paramagnetic resonance analysis has found two types of paramagnetic ions in the nanocomposite. Mössbauer spectra showed the existence of antiferromagnetic and paramagnetic spin structure in the nanocomposite. The CuFeS2/TiO2 nanocomposite showed the highest discoloration activity with a MO conversion of ~ 74% after 120 min irradiation. This study has shown the possibility to prepare nanocomposite material with enhanced photocatalytic activity of decoloration of MO in the visible range by an environmentally friendly manner.
ABSTRACT
CdS/ZnS nanocomposites have been prepared by a two-step solid-state mechanochemical synthesis. CdS has been prepared from cadmium acetate and sodium sulfide precursors in the first step. The obtained cubic CdS (hawleyite, JCPDS 00-010-0454) was then mixed in the second step with the cubic ZnS (sphalerite, JCPDS 00-005-0566) synthesized mechanochemically from the analogous precursors. The crystallite sizes of the new type CdS/ZnS nanocomposite, calculated based on the XRD data, were 3-4 nm for both phases. The synthesized nanoparticles have been further characterized by high-resolution transmission electron microscopy (HRTEM) and micro-photoluminescence (µPL) spectroscopy. The PL emission peaks in the PL spectra are attributed to the recombination of holes/electrons in the nanocomposites occurring in depth associated with Cd, Zn vacancies and S interstitials. Their photocatalytic activity was also measured. In the photocatalytic activity tests to decolorize Methyl Orange dye aqueous solution, the process is faster and its effectivity is higher when using CdS/ZnS nanocomposite, compared to single phase CdS. Very low cytotoxic activity (high viability) of the cancer cell lines (selected as models of living cells) has been evidenced for CdS/ZnS in comparison with CdS alone. This fact is in a close relationship with Cd(II) ions dissolution tested in a physiological solution. The concentration of cadmium dissolved from CdS/ZnS nanocomposites with variable Cd:Zn ratio was 2.5-5.0 µg.mL(-1), whereas the concentration for pure CdS was much higher - 53 µg.ml(-1). The presence of ZnS in the nanocrystalline composite strongly reduced the release of cadmium into the physiological solution, which simulated the environment in the human body. The obtained CdS/ZnS quantum dots can serve as labeling media and co-agents in future anti-cancer drugs, because of their potential in theranostic applications.