ABSTRACT
This work investigates polyvinylidene fluoride (PVDF) membrane modification to enhance its hydrophilicity and antibacterial properties. PVDF membranes were coated with nanoparticles of titanium dioxide (TiO2-NP) and silver (AgNP) at different concentrations and coating times and characterized for their porosity, morphology, chemical functional groups and composition changes. The results showed the successfully modified PVDF membranes containing TiO2-NP and AgNP on their surfaces. When the coating time was increased from 8 to 24 h, the compositions of Ti and Ag of the modified membranes were increased from 1.39 ± 0.13 to 4.29 ± 0.16 and from 1.03 ± 0.07 to 3.62 ± 0.08, respectively. The water contact angle of the membranes was decreased with increasing the coating time and TiO2-NP/AgNP ratio. The surface roughness and permeate fluxes of coated membranes were increased due to increased hydrophilicity. Antimicrobial and antifouling properties were investigated by the reduction of Escherichia coli cells and the inhibition of biofilm formation on the membrane surface, respectively. Compared with that of the original PVDF membrane, the modified membranes exhibited antibacterial efficiency up to 94% against E. coli cells and inhibition up to 65% of the biofilm mass reduction. The findings showed hydrophilic improvement and an antimicrobial property for possible wastewater treatment without facing the eminent problem of biofouling.
ABSTRACT
In this study, we report the effect of the commercial nanoscale zerovalent iron (nZVI) on environmental bacteria, emphasizing the importance of nZVI-bacterial membrane interaction on nZVI toxicity as well as the adaptability of bacteria to nZVI. Exposure of Pseudomonas putida F1 to 0.1, 1.0, and 5.0 g/L of nZVI caused the reduction in colony forming units (CFUs) substantially for almost 3 orders of magnitude. However, a rebound in the cell number was observed after the prolonged exposure except for 5.0 g/L nZVI at which bacterial viability was completely inhibited. Upon exposure, nZVI accumulated on and penetrated into the bacterial cell membrane. Cell membrane composition analysis revealed the conversion of the cis to trans isomer of unsaturated fatty acid upon short-term nZVI exposure, resulting in a more rigid membrane counteracting the membrane-fluidizing effect of nZVI. Several cycles of repetitive exposure of cells to 0.1 g/L nZVI induced a persistent phenotype of P. putida F1 as indicated by smaller colony morphology, a more rigid membrane, and higher tolerance to nZVI. A low interaction between nZVI particles and the surface of the nZVI-persistent phenotypic cells reduced the nZVI-induced membrane damage. This study unveils the significance of nZVI-membrane interaction on toxicity of nZVI toward bacteria.