A Comparison of the Compositional, Microstructural, and Mechanical Characteristics of Ni-Free and Conventional Stainless Steel Orthodontic Wires.

Ni-free orthodontic wires were introduced to mitigate concerns associated with the use of Ni-containing alloys in orthodontics. However, limited information is available on their properties and therefore, the aim of this study was to characterize the elemental composition, the microstructure, and the mechanical properties of Ni-free orthodontic wires and compare them with their stainless steel (SS) counterparts. Four Ni-free and four conventional SS wires were included in this study. All the wires were initially imaged with a Scanning Electron Microscopy (SEM) and their elemental compositions were determined by X-ray Energy Dispersive Spectroscopy (EDX). Then, their microstructure was assessed by X-ray Diffraction (XRD) and the indentation modulus, elastic index, Martens Hardness and Vickers Hardness by Instrumented Indentation Testing (IIT). All the wires demonstrated surface cracks and pores oriented parallel to their long axis. The elemental composition of Ni-free alloys showed an increased Mn and Cr content while both SS and Ni-free wires shared the same dominant austenite structure. In conclusion, despite the differences in elemental composition, Ni-free wires demonstrated a similar microstructure and comparable mechanical properties with their conventional SS counterparts and thus may be considered as a promising alternative for patients with Ni supersensitivity.

Surface and cross-sectional characterization of titanium-nitride coated nickel-titanium endodontic files.

BACKGROUND/PURPOSE: Although the effect of experimental surface modifications on various properties (e.g., fatigue, wear) on coated files have been tested in the past, there is no report for the coating quality of commercially available TiN coated files. The aim of this study was to characterize the surface and cross section of TiN coated endodontic files. MATERIALS AND METHODS: TiN coated nickel-titanium endodontic files (EasyShape) were surface and cross-sectionally analyzed via scanning electron microscopy backscattered electron imaging and energy-dispersive X-ray spectroscopy analysis in spot, area, and line scan modes. RESULTS: Surface imaging revealed parallel oblong regions with higher mean atomic contrast, a finding attributed to increased Ni content. Cross-sectional analysis showed that the coating's average total thickness was 0.31 µm and consisted of a thin layered film. Energy-dispersive X-ray spectroscopy analysis revealed the presence of Ti, Ni, N, and O in the coating, whereas only Ni and Ti were identified in the bulk of the file. Ti and O showed their peak compositions at the bulk/coating and coating/surface interfaces, respectively, whereas N displayed a rather constant content within the coated region. The N and O contents started increasing inner to the coating/bulk interface, denoting possible diffusion of both elements to the subcoating region. CONCLUSION: Surface and bulk characterization showed no uncoated areas of the files tested. Apart from Ti, Ni, and N, oxygen was also identified within the coating region.

Selective Laser Melting Technique of Co-Cr Dental Alloys: A Review of Structure and Properties and Comparative Analysis with Other Available Techniques.

PURPOSE: The aim of this study was to review the effect of selective laser melting (SLM) procedure on the properties of dental structures made of Co-Cr alloys and to evaluate its quality and compare it to those produced by conventional casting and milling fabrication techniques. MATERIALS AND METHODS: A computerized database search using PubMed and Scopus was conducted for peer-reviewed scientific research studies regarding the use of SLM in Co-Cr dental alloys with no restrictions for publication years. The search engines provided hundreds of results, and only 48 scientific research papers, case studies, or literature reviews were considered relevant for this review. RESULTS: The innovative manufacturing concept of SLM offers many advantages compared with casting and milling fabrication techniques. SLM provides different microstructure from casting and milling with minimal internal porosity and internal fitting, marginal adaptation, and comparable bond strength to porcelain. Mechanical and electrochemical properties of SLM structures are enhanced compared to cast, while clinical longevity of single-metal ceramic crowns is comparable to Au-Pt dental alloy. CONCLUSION: The SLM technique provides dental prosthetic restorations more quickly and less expensively without compromising their quality compared with restorations prepared by casting and milling techniques. CLINICAL SIGNIFICANCE: The current SLM devices provide metallic restorations made of Co-Cr alloys for removable and fixed partial dentures without compromising the alloy or restoration properties at a fraction of the time and cost, showing great potential to replace the aforementioned fabrication techniques in the long term; however, further clinical studies are essential to increase the acceptance of this technology by the worldwide dental community.

Effect of Nd:YAG laser parameters on the penetration depth of a representative Ni-Cr dental casting alloy.

The effects of voltage and laser beam (spot) diameter on the penetration depth during laser beam welding in a representative nickel-chromium (Ni-Cr) dental alloy were the subject of this study. The cast alloy specimens were butted against each other and laser welded at their interface using various voltages (160-390 V) and spot diameters (0.2-1.8 mm) and a constant pulse duration of 10 ms. After welding, the laser beam penetration depths in the alloy were measured. The results were plotted and were statistically analyzed with a two-way ANOVA, employing voltage and spot diameter as the discriminating variables and using Holm-Sidak post hoc method (a = 0.05). The maximum penetration depth was 4.7 mm. The penetration depth increased as the spot diameter decreased at a fixed voltage and increased as the voltage increased at a fixed spot diameter. Varying the parameters of voltage and laser spot diameter significantly affected the depth of penetration of the dental cast Ni-Cr alloy. The penetration depth of laser-welded Ni-Cr dental alloys can be accurately adjusted based on the aforementioned results, leading to successfully joined/repaired dental restorations, saving manufacturing time, reducing final cost, and enhancing the longevity of dental prostheses.

Effects of surface treatment and artificial aging on the shear bond strength of orthodontic brackets bonded to four different provisional restorations.

OBJECTIVE: To evaluate the combined effects of material type, surface treatment, and thermocycling on the bond strength of orthodontic brackets to materials used for the fabrication of provisional crowns. MATERIALS AND METHODS: Four materials were included in this study (ProTemp, Trim Plus, Trim II, and Superpont C+B). Sixty cylindrical specimens (1 × 3 cm) were prepared from each material and equally divided into three groups. The first group was ground with silica carbide paper, the second was polished with pumice, and the last group was sandblasted with 50-µm aluminum oxide particles. Stainless-steel maxillary central incisor brackets (Victory Series, 3M) were bonded to the provisional material specimens with Transbond XT light-cured composite resin, and half of the specimens from each group were thermocycled 500 times in 5°C and 55°C water baths. Then the brackets were debonded with shear testing, and the results were statistically analyzed by three-way analysis of variance and Tukey's multiple-comparison tests at α  =  0.05. Adhesive Remnant Index (ARI) was also identified. RESULTS: Before and after thermocycling, ProTemp materials showed the highest shear bond strength with orthodontic brackets (10.3 and 13.1 MPa, respectively). The statistical analysis indicated an interaction among the three independent variables (P < .05) and statistically significant differences in bond strength among provisional materials (P < .001), surface treatments (P < .001), and thermocycling (P < .05). According to the ARI, most groups demonstrated adhesive failure. CONCLUSIONS: The provisional material type, surface treatment, and artificial aging have a significant effect on bond strength. Sandblasting treatment exerts a beneficial effect on shear bond strength.