Engineering of Porphyrin Molecules for Use as Effective Cathode Interfacial Modifiers in Organic Solar Cells of Enhanced Efficiency and Stability.

In the present work, we effectively modify the TiO2 electron transport layer of organic solar cells with an inverted architecture using appropriately engineered porphyrin molecules. The results show that the optimized porphyrin modifier bearing two carboxylic acids as the anchoring groups and a triazine electron-withdrawing spacer significantly reduces the work function of TiO2, thereby reducing the electron extraction barrier. Moreover, the lower surface energy of the porphyrin-modified substrate results in better physical compatibility between the latter and the photoactive blend. Upon employing porphyrin-modified TiO2 electron transport layers in PTB7:PC71BM-based organic solar cells we obtained an improved average power conversion efficiency up to 8.73%. Importantly, porphyrin modification significantly increased the lifetime of the devices, which retained 80% of their initial efficiency after 500 h of storage in the dark. Because of its simplicity and efficacy, this approach should give tantalizing glimpses and generate an impact into the potential of porphyrins to facilitate electron transfer in organic solar cells and related devices.

Low Work Function Lacunary Polyoxometalates as Electron Transport Interlayers for Inverted Polymer Solar Cells of Improved Efficiency and Stability.

Effective interface engineering has been shown to play a vital role in facilitating efficient charge-carrier transport, thus boosting the performance of organic photovoltaic devices. Herein, we employ water-soluble lacunary polyoxometalates (POMs) as multifunctional interlayers between the titanium dioxide (TiO2) electron extraction/transport layer and the organic photoactive film to simultaneously enhance the efficiency, lifetime, and photostability of polymer solar cells (PSCs). A significant reduction in the work function (WF) of TiO2 upon POM utilization was observed, with the magnitude being controlled by the negative charge of the anion and the selection of the addenda atom (W or Mo). By inserting a POM interlayer with ∼10 nm thickness into the device structure, a significant improvement in the power conversion efficiency was obtained; the optimized POM-modified poly[[4,8-bis[(2-ethylhexyl)oxy]benzo[1,2-b:4,5-b']dithiophene-2,6-diyl][3-fluoro-2-[(2- 33 ethylhexyl)carbonyl]thieno[3,4-b]thiophenediyl]]:[6,6]-phenyl-C70 butyric acid methyl ester (PTB7:PC70BM)-based PSCs exhibited an efficiency of 8.07%, which represents a 21% efficiency enhancement compared to the reference TiO2 cell. Similar results were obtained in POM-modified devices based on poly(3-hexylthiophene) (P3HT) with electron acceptors of different energy levels, such as PC70BM or indene-C60 bisadduct (IC60BA), which enhanced their efficiency up to 4.34 and 6.21%, respectively, when using POM interlayers; this represents a 25-33% improvement as compared to the reference cells. Moreover, increased lifetime under ambient air and improved photostability under constant illumination were observed in POM-modified devices. Detailed analysis shows that the improvements in efficiency and stability synergistically stem from the reduced work function of TiO2 upon POM coverage, the improved nanomorphology of the photoactive blend, the reduced interfacial recombination losses, the superior electron transfer, and the more effective exciton dissociation at the photoactive layer/POM/TiO2 interfaces.