Cyanobacteria Biorefinery - Production of poly(3-hydroxybutyrate) with Synechocystis salina and utilisation of residual biomass.

This study evaluates a biorefinery concept for producing poly(3-hydroxybutyrate) (PHB) with the cyanobacterial strain Synechocystis salina. Due to this reason, pigment extraction and cell disruption were investigated as pre-treatment steps for the harvested cyanobacterial biomass. The results demonstrated that at least pigment removal was necessary to obtain PHB with processable quality (weight average molecular weight: 569-988kgmol-1, melting temperature: 177-182°C), which was comparable to heterotrophically produced PHB. The removed pigments could be utilised as additional by-products (chlorophylls 0.27-1.98mgg-1 TS, carotenoids 0.21-1.51mgg-1 TS, phycocyanin 0-127mgg-1 TS), whose concentration depended on the used nutrient source. Since the residual biomass still contained proteins (242mgg-1 TS), carbohydrates (6.1mgg-1 TS) and lipids (14mgg-1 TS), it could be used as animal feed or converted to biomethane (348 mn3 t-1VS) and fertiliser. The obtained results indicate that the combination of photoautotrophic PHB production with pigment extraction and utilisation of residual biomass offer the highest potential, since it contributes to decrease the environmental footprint of the process and because biomass could be used in a cascading way and the nutrient cycle could be closed.

Multi-methodological investigation of the variability of the microstructure of HPMC hard capsules.

The objective of this study was to analyze differences in the subtle microstructure of three different grades of HMPC hard capsule shells using mechanical, spectroscopic, microscopic and tomographic approaches. Dynamic mechanical analysis (DMA), thermogravimetric analysis (TGA), vibrational spectroscopic, X-Ray scattering techniques as well as environmental scanning electron microscopy (ESEM) and optical coherence tomography (OCT) were used. Two HPMC capsules manufactured via chemical gelling, one capsule shell manufactured via thermal gelling and one thermally gelled transparent capsule were included. Characteristic micro-structural alterations (associated manufacturing processes) such as mechanical and physical properties relevant to capsule performance and processability were thoroughly elucidated with the integration of data obtained from multi-methodological investigations. The physico-chemical and physico-mechanical data obtained from a gamut of techniques implied that thermally gelled HPMC hard capsule shells could offer an advantage in terms of machinability during capsule filling, owing to their superior micro- and macroscopic structure as well as specifically the mechanical stability under dry or humid conditions.