ABSTRACT
Type I collagen, the major organic component of human dentin, plays an important role in regulating the mechanical strength of dentin. Collagen in dentin can be strengthened by heating. We hypothesized that UV irradiation could produce similar strengthening effects and might maintain the strength of dentin after rehydration. Beam-shaped dentin specimens from the crowns of human third molars were subjected to flexural testing. Flexural strengths were two and three times greater than those in the control group after 5 minutes' UV irradiation and heating to 140 degrees C, respectively. After 30 days of rehydration, the heated specimens reverted to their original strength, whereas the UV specimens were 69% stronger than the original. Raman spectra of dental collagen were unchanged after heating, whereas several peaks, including a C-C bond in a proline ring, were amplified by UV irradiation. It is concluded that dentin strengthened by UV irradiation retains strength after rehydration because of chemical changes in collagen.
Subject(s)
Dentin/chemistry , Dentin/radiation effects , Collagen/chemistry , Collagen/radiation effects , Dental Stress Analysis , Dentin/ultrastructure , Desiccation , Hot Temperature , Humans , Pliability , Spectrum Analysis, Raman , Ultraviolet Rays , WaterABSTRACT
The flexural strength of Type I collagen, the major organic component of human dentin, increases with heat. We hypothesized that human dentin can be strengthened by heating, which may help prevent fracture of non-vital teeth after restoration. Beam-shaped dentin specimens were obtained from the crowns of human third molars. The dentinal tubular orientations were arranged to run parallel or perpendicular to loading surfaces. The flexural and microtensile strengths of dentin in the parallel specimens were 2- to 2.4-fold greater after being heated between 110 degrees C and 140 degrees C for 1 hr. The stress intensity factors at fracture also increased after specimens were heated. The x-ray diffraction analyses suggested that shrinking of the lateral packing of the collagen triple-helices from 14 A to 11 A was the probable cause of the strengthening of heated dentin. We conclude that heat treatment strengthens human dentin.