ABSTRACT
The aim of the study was to examine the applicability of bioactive and antibacterial nanoparticles to an experimental adhesive. The adhesive (60 wt% BisGMA, 15 wt% TEGDMA, 25 wt% HEMA) was mixed with combinations of 5 wt% methacryl-functionalized polyhedral oligomeric silsesquioxane (MA-POSS) and one kind of bioactive/antibacterial nanoparticles: 1 wt% core-shell silica-silver nanoparticle (SiO2@Ag), 1 wt% bioactive glass with bismuth (BAG-Bi) or 1 wt% calcium phosphate (CAP). Pure adhesive served as control. The physicochemical (degree of conversion (DC), linear shrinkage (LS), shear and complex viscosity, water sorption (WS), sol fraction (SF)), biological (antimicrobial effect) and bioactive (mineral precipitation) properties were investigated. DC and LS remained unchanged. The combination of BAG-Bi/MA-POSS resulted in a significantly increased WS and SF compared to control. In addition, the combination of CAP/MA-POSS slightly increased the shear viscosity of the adhesive. The addition of the nanoparticles did not influence the antimicrobial effects compared to the pure adhesive. Improved mineral inducing capacity could be detected in all nanoparticle combinations. The combination of bioactive and/or antibacterial nanoparticles showed improved mineral inducing capacity, but no antibacterial properties. The material properties were not or only slightly affected.
ABSTRACT
The use of functionalized dental adhesives that might prevent degradation of the dentin hybrid layer has been proposed. The aim of the study was to characterize the physicochemical properties and the potential to induce mineral precipitation of methacrylate-based resins containing methacryl-functionalized polyhedral oligomeric silsesquioxane (MA-POSS-8). In total, six different compositions of resins based on bisphenol A glycerolate dimethacrylate (BisGMA, 40 to 60 wt.%), triethylene glycol dimethacrylate (TEGDMA, 5 to 35 wt.%) and 2-hydroxyethyl methacrylate (HEMA, 25 or 35 wt.%) were prepared and infiltrated with 5 wt.% MA-POSS-8. Unfilled resins served as control. Degree of conversion, viscosity, Martens hardness, indentation modulus, water sorption, and sol fraction were investigated. Polymerized specimens were examined by SEM/EDX for the presence of Ca/P precipitates after immersion in artificial saliva for 28 days at 37 °C. Statistical analysis was performed with two-way ANOVA and Tukey's post-hoc test (p < 0.05). The degree of conversion ranged from 55.0 to 59.8% and was not affected by the addition of MA-POSS-8. Viscosity ranged from 60.0 to 422.3 mPa*s and was not affected by MA-POSS-8 except for one methacrylate-based resin with 60 wt.% BisGMA. Martens hardness and indentation modulus ranged from 161.3 to 138.1 N/mm2 and 4.2 to 3.9 kN/mm2 and were affected by MA-POSS-8 in only one resin (50 wt.% BisGMA, 25 wt.% TEGDMA, 25 wt.% HEMA). Water sorption was not affected by MA-POSS-8; sol fraction was below the detection limit. Formation of Ca/P precipitates was observed on all specimens of test and control groups. Material properties were not affected adversely by MA-POSS-8 except for slight differences in Martens hardness, indention modulus, viscosity in some groups. However, bioactive properties could not be improved by MA-POSS-8.