Copper and nanostructured anatase rutile and carbon coatings induce adaptive antibiotic resistance.

Contaminated surfaces are vehicles for the spread of infectious disease-causing microorganisms. A strategy to prevent their spread is applying antimicrobial coatings to surfaces. Both nanostructured anatase rutile and carbon (NsARC), a TiO2 formulation, and copper are examples of antimicrobial agents that are used in making or coating door handles and similar surfaces, to reduce microbial loads. Antimicrobial surfaces have been extensively tested for antimicrobial activity but not sublethal effects, such as exposure-associated multiple antibiotic resistance phenotypes usually caused by induction of efflux pump genes. The possibility of NsARC and copper inducing indicative efflux pump pathways was investigated by monitoring the expression of mScarlet fluorescent protein (FP) in two reporter strains of Escherichia coli. There was an increase in the expression of FP in the reporter strains exposed to NsARC and copper relative to the inert control composed of stainless steel. Furthermore we tested E. coli and Staphylococcus aureus following 8 h of exposure to NsARC for changes in resistance to selected antibiotics. E. coli that were exposed to NsARC became more susceptible to kanamycin but there was no significant change in susceptibility of S. aureus to any tested antibiotics. These findings suggests that even though NsARC and copper are antimicrobial, they also have some potential to cause unintended phenotypes.

Antimicrobial and biofilm-disrupting nanostructured TiO2 coating demonstrating photoactivity and dark activity.

Antimicrobial materials are tools used to reduce the transmission of infectious microorganisms. Photo-illuminated titania (TiO2) is a known antimicrobial material. Used as a coating on door handles and similar surfaces, it may reduce viability and colonization by pathogens and limit their spread. We tested the survival of Escherichia coli, Pseudomonas aeruginosa, Staphylococcus aureus and Saccharomyces cerevisiae on a nano-structured TiO2-based thin film, called 'NsARC', and on stainless steel under a variety of light wavelengths and intensities. There was significantly less survival (P <0.001) of all the organisms tested on NsARC compared to inert uncoated stainless steel under all conditions. NsARC was active in the dark and possible mechanisms for this are suggested. NsARC inhibited biofilm formation as confirmed by scanning electron microscopy. These results suggest that NsARC can be used as a self-cleaning and self-sterilizing antimicrobial surface coating for the prevention and reduction in the spread of potentially infectious microbes.

Process-Induced Nanostructures on Anatase Single Crystals via Pulsed-Pressure MOCVD.

The recent global pandemic of COVID-19 highlights the urgent need for practical applications of anti-microbial coatings on touch-surfaces. Nanostructured TiO2 is a promising candidate for the passive reduction of transmission when applied to handles, push-plates and switches in hospitals. Here we report control of the nanostructure dimension of the mille-feuille crystal plates in anatase columnar crystals as a function of the coating thickness. This nanoplate thickness is key to achieving the large aspect ratio of surface area to migration path length. TiO2 solid coatings were prepared by pulsed-pressure metalorganic chemical vapor deposition (pp-MOCVD) under the same deposition temperature and mass flux, with thickness ranging from 1.3-16 mm, by varying the number of precursor pulses. SEM and STEM were used to measure the mille-feuille plate width which is believed to be a key functional nano-dimension for photocatalytic activity. Competitive growth produces a larger columnar crystal diameter with thickness. The question is if the nano-dimension also increases with columnar crystal size. We report that the nano-dimension increases with the film thickness, ranging from 17-42 nm. The results of this study can be used to design a coating which has co-optimized thickness for durability and nano-dimension for enhanced photocatalytic properties.

Nanostructured TiO2 anatase-rutile-carbon solid coating with visible light antimicrobial activity.

TiO2 photocatalyst is of interest for antimicrobial coatings on hospital touch-surfaces. Recent research has focused on visible spectrum enhancement of photocatalytic activity. Here, we report TiO2 with a high degree of nanostructure, deposited on stainless steel as a solid layer more than 10 µm thick by pulsed-pressure-MOCVD. The TiO2 coating exhibits a rarely-reported microstructure comprising anatase and rutile in a composite with amorphous carbon. Columnar anatase single crystals are segmented into 15-20 nm thick plates, resulting in a mille-feuilles nanostructure. Polycrystalline rutile columns exhibit dendrite generation resembling pine tree strobili. We propose that high growth rate and co-deposition of carbon contribute to formation of the unique nanostructures. High vapor flux produces step-edge instabilities in the TiO2, and solid carbon preferentially co-deposits on certain high energy facets. The equivalent effective surface area of the nanostructured coating is estimated to be 100 times higher than standard TiO2 coatings and powders. The coatings prepared on stainless steel showed greater than 3-log reduction in viable E coli after 4 hours visible light exposure. The pp-MOCVD approach could represent an up-scalable manufacturing route for supported catalysts of functional nanostructured materials without having to make nanoparticles.

Delivering sustainable infrastructure that supports the urban built environment.

Sustainable living will require megacity-level infrastructural support designs and paradigms.