ABSTRACT
Sansevieria trifasciata fibre (STF) is a lignocellulosic material which could be utilised for reinforcement composites. Surface modification is often needed to improve the compatibility of hydrophilic STF and hydrophobic resin. In this study, treatments for natural fibres to attain superhydrophobic properties were carried out using silica nanoparticles and fluorosilane. Sansevieria trifasciata fibres (STF) were subjected to treatment by deposition of silica (SiO2) nanoparticles which were prepared by the sol-gel method, then followed by modification with fluorosilane, namely 1H, 1H, 2H, 2H-perfluorooctyltriethoxysilane (PFOTS). The presence of SiO2 nanoparticles and PFOTS were evaluated using Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDX). The crystallisation properties and thermal behaviour of STF were studied through X-ray diffraction (XRD) and thermogravimetric (TGA) analysis, respectively. The hydrophobicity of STF was determined by water contact angle (WCA) measurement. The results show that nanoscale SiO2 particles were deposited on the STF surface, and PFOTS were covalently linked to them. The SiO2 nanoparticles provide surface roughness to the fibres, whereas the long-chain fluorine on PFOTS lowered the surface free energy, and their combination in these treatments has successfully modified the STF surface from hydrophilic into superhydrophobic with a WCA of 150° and sliding angle of less than 10°. Altogether, a non-toxic, simple, and promising method of imparting hydrophobicity on natural fibres was developed, opening new opportunities for these fibres as reinforcement for composite parts.
ABSTRACT
Epoxy nano composites containing micro and nano silica were prepared by varying the filler's weight loading as an attempt to investigate the effects of incorporating these fillers in influencing its mechanical properties. Mechanical properties characterizations include the evaluation of tensile. The mechanical properties of the epoxy composites were found to tremendously increase as both micro and nano silica were added together at a 1:1 wt.% ratio. For example, the highest values of Young's modulus were recorded to be 5.39 GPa for 25 wt.% loading (12.5 wt.% Micro + 12.5 wt.% nano), while Young's modulus values of 5.22 MPa and 5.32 MPa were recorded for micro and nano silica, respectively, at the same weight loading. The most outstanding results were observed at 25 wt.% hybrids (12.5 wt.% micro silica + 12.5 wt.% nano silica), where the values of Young's modulus were increased by 228% compared to the neat epoxy. This study successfully demonstrated synergistic effects demonstrated by combining micro and nano silica fillers, which created an interaction that significantly enhanced the Young's modulus of epoxy composites.