Effect of the Advanced Cranial and Craniofacial Implant Fabrication on Their Degradation Affinity.

Biodegradable craniofacial and cranial implants are a new aspect in terms of reducing potential complications, especially in the long term after surgery. They are also an important contribution in the field of surgical reconstructions for children, for whom it is important to restore natural bone in a relatively short time, due to the continuous growth of bones. The aim of this study was to verify the impact of the technology on biodegradability and to estimate the risk of inappropriate implant resorption time, which is an important aspect necessary to select prototypes of implants for in vivo testing. Prototypes of implants were made using two technologies: 3D printing using a PLDLA: poly(L-co-D,L lactide) (PLDLA) filament containing hydroxyapatite nanoparticles, and injection using PLDLA. After the radiation sterilization process, they were subjected to in vitro degradation under accelerated conditions. As part of this study, the in vitro degradation of newly developed biodegradable implant technologies was assessed in accordance with the guidelines of European standards. It was found that the implant manufacturing process had a significant impact on the degradation time under simulated conditions in various media. Implants made using the injection technique were characterized by lower susceptibility to degradation media compared to the 3D-printed implant under accelerated conditions.

Effect of Sterilization on Bone Implants Based on Biodegradable Polylactide and Hydroxyapatite.

Medical devices intended for implantation must be, in accordance with the legal provisions in force in the European Union, sterile. The effect of sterilization on the structural and thermal properties of implants, made by 3D printing from biodegradable polylactide and hydroxyapatite in a proportion of 9/1 by weight, was evaluated. The implants were sterilized using three different methods, i.e., steam sterilization, ethylene oxide sterilization, and electron beam radiation sterilization. As a result of the assessment of the structural properties of the implants after sterilization, a change in the molecular weight of the raw material of the designed implants was found after each of the performed sterilization methods, while maintaining similar characteristics of the thermal properties and functional groups present.

Fragment-Resistant Property Optimization within Ballistic Inserts Obtained on the Basis of Para-Aramid Materials.

A high protection level without an excessive weight is a basic assumption in the design of modern armors and protection systems. Optimizing armors is a task of development of the utmost importance, and is the subject of the work contained within this article. Optimization of ballistic inserts was carried out using multicriterial analysis (MCA), which enables the selection of the optimal composition, taking into account properties such as ballistic resistance, physicomechanical, and/or functional properties. For this purpose, various types of composite systems were produced and tested in terms of their fragment-resistant properties according to STANAG 2920 and the composite areal density of different ballistic inserts: Soft inserts made of Twaron® para-aramid sheets, hard ballistic inserts made of multilayer hot-pressed preimpregnated sheets, and hybrid hard ballistic inserts prepared on the basis of multilayer hot-pressed preimpregnated sheets and ceramics. The application of MCA and performance of experimental fragment resistance tests for a wide spectrum of para-aramid inserts are part of the novelty of this work. The obtained test results showed that depending on the composition of the composite system, we could obtain a wide range of fragmentation resistance in the range of 300 to >1800 m/s, which depended on the areal density and type of composite system used. The results also confirmed that MCA is a good computational tool to select the optimal design of para-aramid ballistic inserts.