ABSTRACT
In this study, the removal efficiency of endosulfan as a persistent organic pollutant and formation of its metabolites were investigated using Ag/TiO2/Fe3O4 photocatalyst under visible and UV-A light. Light intensity, catalyst amount, initial endosulfan concentration, initial pH and time were determined as controllable factors for Taguchi experimental design. The highest removal efficiencies of endosulfan were achieved as 86.14% and 85.46% for visible and UV-A light sources, respectively. According to the greatest best criterion, the level at which the highest S/N ratio was obtained for each parameter was accepted as the optimum value. As a result of the validation experiments, 94.2% and 91.9% efficiency were obtained for visible and UV-A light, respectively. The metabolite formations of endosulfan (endosulfan sulfate, ether, and lactone) remained below 7% in all experiments on a concentration basis. In the reuse experiments of the magnetically recovered photocatalyst, high removal efficiency of around 80% was obtained after four cycles. The removal efficiencies were found to be 86.7% and 84.8%, for real samples taken from the drinking water treatment plant inlet and the spring water network injected with endosulfan under optimal photocatalysis experimental conditions, respectively. It has been shown that nitrate and sulfate anions, which are in significant concentrations in raw water samples, have very little effects on endosulfan removal. The overall results showed that the Ag/TiO2/Fe3O4 photocatalyst was produced successfully, the catalyst was highly effective in the mineralization of endosulfan in synthetic and real water samples under UV and visible light, and effective yields could be obtained even with reuse. Supplementary information: The online version contains supplementary material available at 10.1007/s40201-023-00864-z.
ABSTRACT
In this study the magnetic nanocomposite material was synthesized with Fe3O4 impregnated to sugar beet pulp using chemical precipitation technique. Ni(II) removal performance of magnetic nanocomposite was investigated under different environmental conditions such as contact time, adsorbent dose, pH, initial heavy metal concentration, etc. The experimental studies have shown that, 81.2% Ni(II) removal efficiency was achieved at optimal conditions (25 mg/L initial Ni(II) concentration at 40 minute contact time, 200 rpm shaking speed, 5 g/L nanocomposite dose and pH 6.6). Freundlich and Langmuir isotherm experiments were performed and correlation coefficients were determined as 94.5% and 99.4%, respectively. The maximum adsorption capacity of material was achieved as 9.36 mg/g. These findings indicate that the adsorption that takes place is a monolayer process. The results of the pseudo-second order kinetic model (R2 = 0.9947) indicate the chemisorptions process is used for Ni(II) removal using the electrostatic interaction. Thermodynamic studies illustrated that Ni(II) adsorption onto nanocomposite are exothermic and causes a decrease in the entropy. The adsorption of Ni(II) ions is non-spontaneous except for at low temperature and low initial concentrations. Nanocomposite characterization was illuminated with XRD, FT-IR, BET, TGA, TEM, SEM/EDX analysis.
In this study, it was aimed to synthesis new adsorbent using sugar beet pulp together with Fe3O4 under suitable conditions, obtain a magnetic nanocomposite, and examine the reusability and recovery properties of the produced material. The use of industrial wastes as an adsorbent material provides both a solution to the problem of the removal of wastes and a reuse method for the use of wastes as a low cost adsorbent for a useful purpose. Therefore, it has two advantages: There is a need to investigate the feasibility of investigating all possible industry-based cheap adsorbent sources as well as the removal of heavy metals for the production of a reliable and harmless adsorbent.