Understanding the complexity of deinking plastic waste: An assessment of the efficiency of different treatments to remove ink resins from printed plastic film.

Plastic packaging is usually heavily printed with inks to provide functional benefits. However, the presence of inks strongly impedes the closed-loop recycling of plastic films. Various media have already been studied for the deinking of plastic films, but there is little scientific insight into the effectiveness of different deinking techniques. Therefore, this study aims to obtain a systematic understanding by measuring the liquefaction and maximum solubility of 14 chemically different polymer resins in seven different media typically used in plastic deinking, such as acetone, ethyl acetate, sodium hydroxide solution, cetyltrimethylammonium bromide solution, formic acid, sulfuric acid, and N,N-dimethylcyclohexylamine. Our findings show that acid-based media are able to remove a broader range of polymer resins. Organic solvents are particularly effective against acrylics and related polymer resins. The deinking efficiency tests on pure resins are also confirmed by deinking four printed plastic films containing different classes of polymer resins. A basic cost and environmental impact analysis is given to evaluate scale-up potential of the deinking medium.

Towards a Better Understanding of Delamination of Multilayer Flexible Packaging Films by Carboxylic Acids.

Recycling multilayer plastic packaging is challenging due to its intrinsic compositional heterogeneity. A promising route to increase recycling rates for these materials is delamination, which allows recycling the polymers separately. Yet, this process is not well understood on a fundamental level. This study aimed to obtain first principles-based insights of the delamination mechanism of multilayer flexible packaging film (MFPF) with carboxylic acids. Delamination of MFPFs was described through a model based on Fick's first law of diffusion and first-order dissolution kinetics of polyurethane adhesives. The model was experimentally tested on 5 different MFPFs at different temperatures (50-75 °C), formic acid concentrations (50-100 vol %), and solid/liquid (S/L) ratios (0.005, 0.025, and 0.12 g mL-1 ). Under the studied conditions the model proved to successfully estimate the delamination time of MFPF with the average Theil's Inequality Coefficient (TIC) value of 0.14. Essential for scaling-up delamination processes is the possibility to use high S/L ratios as the solubility of the adhesive is rarely limiting.