Rapid additive manufacturing of an obturator prosthesis with the use of an intraoral scanner: A dental technique.

A protocol for a completely digital manufacturing process for an obturator prosthesis is described. An intraoral scanner was used to capture the mandible and maxilla together with the sinus defect. The obturator base and the artificial teeth were created with a computer-aided design software program and manufactured by 3-dimensional printing. Stainless steel clasps provided the retention for the prosthesis.

Bonding Interface and Repairability of 3D-Printed Intraoral Splints: Shear Bond Strength to Current Polymers, with and without Ageing.

This in-vitro study investigates the bonding interfaces reached by the conditioning of a splint material additively manufactured by digital light processing (AM base) as well as the shear bond strength (SBS) of resins bonded to these surfaces (repair material). Therefore, the AM base was either stored in dry for 12 h or wet environment for 14 days to simulate ageing by intraoral wear. The dry and wet group was bonded after physical and/or chemical conditioning to cylinders made from polymethylmethacrylate or four novel polymers allowing splint modifications. Blasted and methylmethacrylate (MMA)-conditioned Polymethylmethacrylate (PMMA) bonded to PMMA acted as the gold standard. The surface profiles revealed highest differences of Ra towards the gold standard in AM base conditioned with other than MMA after sandblasting. The adhesively bonded repair materials of the wet AM base were further aged in wet environment for 14 days. The SBS of the gold standard (25.2 MPa and 25.6 MPa) was only reached by PMMA bonded to blasted and MMA-conditioned AM base after dry (22.7 MPa) and non-conditioned after wet storage (23 MPa). Four repair materials failed to reach the threshold of 5 MPa after dry storage and three after wet storage, respectively. Non-conditioned AM base revealed the highest risk for adhesive fractures when using other resins than PMMA.

Polishability and wear resistance of splint material for oral appliances produced with conventional, subtractive, and additive manufacturing.

Occlusal splints to treat bruxism are commonly made from polymethylmethacrylate (PMMA) in a manual workflow (powder-liquid technique). Today digitalization allows a machine-based manufacturing in subtractive (milling) and additive (printing) means using industrial-made PMMA or comparable resins. An in-vitro study should assess the surface finish and screen the wear resistance of conventional and industrial materials. Therefore, a total of 30 specimens made from conventionally PMMA (group C; powder-liquid, Palapress), polycarbonate ingots (group S; innoBlanc splint plus), and light-curing resin (group A; VarseoWax splint) were polished to examine the surface roughness (Ra) by profilometry and further analyzed by SEM. The specimens were loaded with a steatite ball moving 5000 times along 1cm with 5N of surface pressure under constant wetting (artificial saliva). The total height of profile (Pt) was calculated by further profilometry of the specimens. All specimen showed initially comparable Ra values ranging between 0.06 and 0.05µm (SD = 0.01) after polishing. SEM investigations revealed no visual cues for scratches or irregularities in any group. After abrasion test, the comparison of the wear depths, revealed mean Pt values of 111.4µm (SD = 18.5) in C, 85.7µm (SD = 21.5) in S, and 99.1µm (SD = 21.5) in A, whereas the mean of S was statistically different from C (p = 0.025). No signs of abrasion were found on the steatite balls. All materials showed comparable polished surfaces and a similar scale of wear. It remains questionable if the detected statistical differences are of clinical relevance, but indicates the need for tests of novel materials, especially in additive manufacturing.