Exploring the Limits: Degradation Behavior of Lead Halide Perovskite Films under Exposure to Ultrahigh Doses of γ Rays of Up to 10 MGy.

Herein, we show that thin films of MAPbI3, FAPbI3, (CsMA)PbI3, and (CsMAFA)PbI3, where MA and FA are methylammonium and formamidinium cations, respectively, tolerate ultrahigh doses of γ rays approaching 10 MGy without significant changes in their absorption spectra. However, among the studied materials, FAPbI3 was the only one that did not form metallic lead due to its extreme radiation hardness. Infrared near-field optical microscopy revealed the radiation-induced depletion of organic cations from the grains of MAPbI3 and their accumulation at the grain boundaries, whereas FAPbI3 on the contrary lost FA cations from the grain boundaries. The multication (CsMAFA)PbI3 perovskite underwent a facile phase segregation to domains enriched with MA and FA cations, which is a principally new radiation-induced degradation pathway. Our findings suggest that the radiation hardness of the rationally designed perovskite semiconductors could go far beyond the impressive threshold of 10 MGy we set herein for FAPbI3 films, which opens many exciting opportunities for practical implementation of these materials.

Cellulose from Annual Plants and Its Use for the Production of the Films Hydrophobized with Tetrafluoroethylene Telomers.

Cellulose HogC was produced by the modified traditional method with 35% yield from the stem of Sosnovsky hogweed and was characterized by elemental analysis, infrared (IR) spectroscopy, powder X-ray diffractometry, differential scanning calorimetry (DSC) and X-ray photoelectron spectroscopy (XPS). For HogC, the degree of crystallinity (approximately 70%) and the glass transition temperature (105-108 °C) were determined. It was found that the whiteness characteristic in the case of HogC was 92% and this significate was obtained without a bleaching procedure using chlorine-containing reagents. In this paper, the possibility of hydrophobization of HogC films by treatment with radiation-synthesized telomers of tetrafluoroethylene is shown. It was found that the contact angle of the telomer-treated cellulose film surface depended on the properties of the telomers (the chemical nature of the solvent, and the initial concentration of tetrafluoroethylene) and could reach 140 degrees.

Multifunctional Compound Combining Conductivity and Single-Molecule Magnetism in the Same Temperature Range.

We report the first highly conducting single-molecule magnet, (BEDO)4[ReF6]·6H2O [1; BEDO = bis(ethylenedioxo)tetrathiafulvalene], whose conductivity and single-molecule magnetism coexist in the same temperature range. The compound was synthesized by BEDO electrocrystallization in the presence of (Ph4P)2[ReF6]·2H2O and characterized by crystallography and measurements of the conductivity and alternating-current magnetic susceptibility.