ABSTRACT
In this study, the surface modification of Santa Barbara Amorphous-16 (SBA-16) with aluminum (SBA-16-Al) was carried out as a rifampicin matrix for the treatment of tuberculosis. Surface modification of SBA-16 was achieved using the direct-synthesis grafting method. Then, the adsorption and release properties of rifampicin from the SBA-16-Al matrix have been studied in batches. In addition, the SBA-16-Al has been characterized using Fourier-Transform Infrared Spectroscopy (FTIR), X-ray diffraction analysis (XRD), transmission electron microscopy (TEM), and Surface Area Analysis (SAA) Brunaur, Emmett and Teller (SAA-BET). The results show that the mesoporous material, the SBA-16-Al has a specific surface area of 843.5 m2 g-1 and 624.3 m2 g-1 for SBA-16, nanometer-sized pore diameters, and an amorphous crystal lattice. The FTIR spectra showed the Al-O bond at 802 cm-1 which indicates the Al group has been successfully added into SBA-16. The adsorption isotherm of rifampicin in SBA-16-Al follows the Freundlich model which illustrates the adsorption is heterogeneous and forms a multilayer. The adsorption of rifampicin is chemisorption which occurs non-spontaneously and is quite stable. The release kinetics of rifampicin in the drug delivery system followed the Higuchi model with k1 0.5472 mg 0.5/hour pH 1.5 and k2 mg 0.5/hour pH 6.5.
ABSTRACT
This study explores the modification of lignin with surfactants, which can be used as a template to make mesoporous structures, and can also be used in combination with manganese oxide to produce manganese oxide/lignin-derived carbon. Organosolv extraction, using ethanol (70%) at 150 °C, was carried out to extract lignin from oil palm wood. Lignin was then mixed with Pluronic F-127, with and without Mn(NO3)2, and then crosslinked with acidic formaldehyde, resulting in a carbon precursor-based modified lignin. Carbonization was carried out at 900 °C to produce lignin-derived carbon and manganese oxide/lignin-derived carbon. The characterization materials included Fourier transform infrared (FTIR) spectroscopy, scanning electron microscope-energy dispersive X-ray (SEM-EDX) mapping, X-ray diffraction (XRD), and N2-sorption analysis. FTIR curves displayed the vibration bands of lignin and manganese oxide. SEM images exhibited the different morphological characteristics of carbon from LS120% (lignin with a Pluronic surfactant of 120%) and LS120%Mn20% (lignin with a Pluronic of 120% and Mn oxide of 20%). Carbon LS120% (C-LS120%) showed the highest specific surface area of 1425 m2/g with a mean pore size of 3.14 nm. The largest mean pore size of 5.23 nm with a specific surface area of 922 m2/g was exhibited by carbon LS120%-Mn20% (C-LS120%-Mn20%). C-LS120%Mn20% features two phases of Mn oxide crystals. The highest specific capacitance of 345 F/g was exhibited by C-LS120%-Mn20%.