ABSTRACT
The impact of the progressive addition of ZnO up to 5 mol% on the thermal, structural, and optical properties of Er3+-doped phosphate glasses within the system NaPO3-NaF-ZnO-Ag2O is discussed. The glass network was found to depolymerize upon the addition of ZnO. This promotes a slight increase in the intensity of the emission at 1.5 µm as well as enhances the silver ions clustering ability under the heat treating. The Ag-nanoparticles formed after moderate heat-treatment can further enhance the emission at 1.5 µm, whereas an excessive amount of the clusters leads to the opposite effect. The addition of ZnO helps to slightly increase the glass ability of the system. The crystallization behavior study revealed that surface crystallization is observed for all the glasses. It is found that even a small ZnO addition changes the crystalline phases formed after devitrification. Moreover, the addition of ZnO decreases the crystallization tendency of the glass.
ABSTRACT
Glasses with the system (84.60-x) NaPO3-5 ZnO-(9.40-x) NaF-x Ag2O-1 Er2O3, (x = 0, 2, 4, and 6) (mol%) were synthesized by the conventional melt-quenching method. The impact of the addition of Ag2O on the physical, thermal, structural, and optical properties of the glasses is discussed. The Judd-Oflet analysis was used to evaluate the radiative properties of the emission transitions of the glasses. The enhancement of luminescence properties due to Ag2O is discussed in terms of consequent changes in the local electromagnetic field, symmetry, and the ligand field around the Er3+ ion. The heat treatment of the glass was performed in order to precipitate Ag nanoparticles (NPs), which form as a layer at the surface of the heat-treated glasses as confirmed using scanning electron microscopy (SEM). The Ag NPs were found to increase the intensity of the emission at 1.5 µm.