Dense arrays of cobalt nanorods as rare-earth free permanent magnets.

We demonstrate in this paper the feasibility to elaborate rare-earth free permanent magnets based on cobalt nanorods assemblies with energy product (BH)max exceeding 150 kJ m(-3). The cobalt rods were prepared by the polyol process and assembled from wet suspensions under a magnetic field. Magnetization loops of dense assemblies with remanence to a saturation of 0.99 and squareness of 0.96 were measured. The almost perfect M(H) loop squareness together with electron microscopy and small angle neutron scattering demonstrate the excellent alignment of the rods within the assemblies. The magnetic volume fraction was carefully measured by coupling magnetic and thermogravimetric analysis and found in the range from 45 to 55%, depending on the rod diameter and the alignment procedure. This allowed a quantitative assessment of the (BH)max values. The highest (BH)max of 165 kJ m(-3) was obtained for a sample combining a high magnetic volume fraction and a very large M(H) loop squareness. This study shows that this bottom-up approach is very promising to get new hard magnetic materials that can compete in the permanent magnet panorama and fill the gap between the ferrites and the NdFeB magnets.

Tuning deposition of magnetic metallic nanoparticles from periodic pattern to thin film entrainment by dip coating method.

In this work, we report on the self-assembly of bimetallic CoFe carbide magnetic nanoparticles (MNPs) stabilized by a mixture of long chain surfactants. A dedicated setup, coupling dip coating and sputtering chamber, enables control of the self-assembly of MNPs from regular stripe to continuous thin films under inert atmosphere. The effects of experimental parameters, MNP concentration, withdrawal speed, amount, and nature of surfactants, as well as the surface state of the substrates are discussed. Magnetic measurements revealed that the assembled particles were not oxidized, confirming the high potentiality of our approach for the controlled deposition of highly sensitive MNPs.

A frequency-adjustable electromagnet for hyperthermia measurements on magnetic nanoparticles.

We describe a low-cost and simple setup for hyperthermia measurements on colloidal solutions of magnetic nanoparticles (ferrofluids) with a frequency-adjustable magnetic field in the range of 5-500 kHz produced by an electromagnet. By optimizing the general conception and each component (nature of the wires, design of the electromagnet, etc.), a highly efficient setup is obtained. For instance, in a useful gap of 1.1 cm, a magnetic field of 4.8 mT is generated at 100 and 500 kHz with output powers of 3.4 and 75 W, respectively. A maximum magnetic field of 30 mT is obtained at 100 kHz. The temperature of the colloidal solution is measured using optical fiber sensors. To remove contributions due to heating of the electromagnet, a differential measurement is used. In this configuration the sensitivity is better than 1.5 mW at 100 kHz and 19.3 mT. This setup allows one to measure weak heating powers on highly diluted colloidal solutions. The hyperthermia characteristics of a solution of Fe nanoparticles are described, where both the magnetic field and the frequency dependence of heating power have been measured.

Magnetic configurations of 30 nm iron nanocubes studied by electron holography.

Ferromagnetic nanomaterials exhibit unique magnetic properties common to materials with dimensions approaching the atomic scale and have potential applications in magnetic data storage. Technological applications, however, require that the detailed magnetic behaviors and configurations of individual and interacting magnetic nano-objects be clarified. We determined the magnetic remnant configurations in single crystalline 30 nm Fe nanocubes and groups of nanocubes using off-axis electron holography in a transmission electron microscope. Our measurements on an isolated cube reveal a vortex state whose core size has been determined. Two neighboring nanocubes with adjacent {100} surfaces exhibit a ferromagnetic dipolar coupling, while similar magnetic interactions between four cubes in a square arrangement induce a bending of the magnetic induction, i.e., a magnetic flux closure state. The various configurations were successfully simulated by micromagnetic calculations.