Degradable polyisoprene by radical ring-opening polymerization and application to polymer prodrug nanoparticles.

Radical ring-opening polymerization (rROP) has received renewed attention to incorporate cleavable linkages into the backbones of vinyl polymers, especially from cyclic ketene acetals (CKAs). Among the monomers that hardly copolymerize with CKAs are (1,3)-dienes such as isoprene (I). This is unfortunate since synthetic polyisoprene (PI) and its derivatives are the materials of choice for many applications, in particular as elastomers in the automotive, sport, footwear, and medical industries, but also in nanomedicine. Thionolactones have been recently proposed as a new class of rROP-compatible monomers for insertion of thioester units in the main chain. Herein, we report the synthesis of degradable PI by rROP via the copolymerization of I and dibenzo[c,e]oxepane-5-thione (DOT). Free-radical polymerization as well as two reversible deactivation radical polymerization techniques were successfully used for the synthesis of (well-defined) P(I-co-DOT) copolymers with adjustable molecular weights and DOT contents (2.7-9.7 mol%). Reactivity ratios of r DOT = 4.29 and r I = 0.14 were determined, suggesting preferential incorporation of DOT in comparison to I. The resulting P(I-co-DOT) copolymers were successfully degraded (from -47% to -84% decrease in M n) under basic conditions. As a proof of concept, the P(I-co-DOT) copolymers were formulated into stable and narrowly dispersed nanoparticles, showing similar cytocompatibility on J774.A1 and HUVEC cells compared to their PI counterparts. Furthermore, Gem-P(I-co-DOT) prodrug nanoparticles were synthesized by the "drug-initiated" method and exhibited significant cytotoxicity on A549 cancer cells. P(I-co-DOT) and Gem-P(I-co-DOT) nanoparticles were degraded under basic/oxidative conditions by bleach and under physiological conditions in the presence of cysteine or glutathione.

RAFT-Mediated Emulsion Polymerization-Induced Self-Assembly for the Synthesis of Core-Degradable Waterborne Particles.

Poly(N-acryloylmorpholine) (PNAM)-decorated waterborne nanoparticles comprising a core of either degradable polystyrene (PS) or poly(n-butyl acrylate) (PBA) were synthesized by polymerization-induced self-assembly (PISA) in water. A PNAM bearing a trithiocarbonate chain end (PNAM-TTC) was extended via reversible addition-fragmentation chain transfer (RAFT)-mediated emulsion copolymerization of either styrene (S) or n-butyl acrylate (BA) with dibenzo[c,e]oxepane-5-thione (DOT). Well-defined amphiphilic block copolymers were obtained. The in situ self-assembly of these polymers resulted in the formation of stable nanoparticles. The insertion of thioester units in the vinylic blocks enabled their degradation under basic conditions. The same strategy was then applied to the emulsion copolymerization of BA with DOT using a poly(ethylene glycol) (PEG) equipped with a trithiocarbonate end group, resulting in PEG-decorated nanoparticles with degradable PBA-based cores.

One-Step Synthesis of Degradable Vinylic Polymer-Based Latexes via Aqueous Radical Emulsion Polymerization.

Aqueous emulsion copolymerizations of dibenzo[c,e]oxepane-5-thione (DOT) were performed with n-butyl acrylate (BA), styrene (S) and a combination of both. In all cases, stable latexes were obtained in less than two hours under conventional conditions; that is in the presence of sodium dodecyl sulfate (SDS) used as surfactant and potassium persulfate (KPS) as initiator. A limited solubility of DOT in BA was observed compared to S, yielding to a more homogeneous integration of DOT units in the PS latex. In both cases, the copolymer could be easily degraded under basic conditions. Emulsion terpolymerization between DOT, BA and S allowed us to produce stable latexes not only composed of degradable chains but also featuring a broad range of glass transition temperatures.