ABSTRACT
This study analysed thermoluminescence (TL) glow curves of the polymer pencil lead graphite (PPLG) due to its potential applications in radiation dosimetry. The TL glow curves provide information on the physical parameters of the defects participating in luminescence process. The glow curves for different diameters PPLG samples were obtained with varying temperature from 50 to 300 °C, at a fixed heating rate of 10 °Cs-1. A number of methods (initial rise, peak shape and curve fitting) were used to fit the TL glow peaks of the PPLG samples obtained under photon dose of 200 Gy. From the fitted TL signals, the trap parameters such as the order of kinetics, the activation energy, the frequency factor, etc. for the individual peaks were numerically determined. The lifetimes of TL process were calculated assuming the first-order kinetics. The results are compared among the different methods adopted in this study. Implications about the possible results in glow curve deconvolution are discussed.
ABSTRACT
Preliminary study has been made of black human hair, carbon concentration of some 53%, a model in examining the potential of hair of the human head in retrospective and emergency biodosimetry applications, also offering effective atomic number near to that of water. The hair samples were exposed to [Formula: see text]Co gamma rays, delivering doses from 0 to 200 Gy. Structural alterations were observed, use being made of Raman and photoluminescence (PL) spectroscopy. Most prominent among the features observed in the first-order Raman spectra are the D and G peaks, appearing at 1370 [Formula: see text] and 1589 [Formula: see text] respectively, the intensity ratio [Formula: see text] indicating dose-dependent defects generation and annealing of structural alterations. The wavelengths of the PL absorption and emission peaks are found to be centred at [Formula: see text] nm and [Formula: see text] nm, respectively. The hair samples mean band gap energy ([Formula: see text]) post-irradiation was found to be [Formula: see text] eV, of the order of a semiconductor and approximately two times the [Formula: see text] of other carbon-rich materials reported via the same methodology.