Anti-thrombogenic properties of a nitric oxide-releasing dextran derivative: evaluation of platelet activation and whole blood clotting kinetics.

Controlling platelet activation and clotting initiated by cardiovascular interventions remains a major challenge in clinical practice. In this work, the anti-thrombotic properties of a polysaccharide-based nitric oxide (NO)-releasing dextran derivative are presented. Total platelet adhesion, platelet morphology and whole blood clotting kinetics were used as indicators to evaluate the anti-clotting properties of this material. With a total NO delivery of 0.203±0.003 µmol, the NO-releasing dextran derivative (Dex-SNO) mixed with blood plasma demonstrated a significantly lower amount of platelet adhesion and activation onto a surface and reduced whole blood clotting kinetics. Nearly 75% reduction in platelet adhesion and a significant retention of platelet morphology were observed with blood plasma treated with Dex-SNO, suggesting this to be a potential anti-platelet therapeutic agent for preventing thrombosis that does not have an adverse effect on circulating platelets.

Nitric oxide releasing Tygon materials: studies in donor leaching and localized nitric oxide release at a polymer-buffer interface.

Tygon is a proprietary plasticized poly(vinyl chloride) polymer that is used widely in bioapplications, specifically as extracorporeal circuits. To overcome issues with blood clot formation and infection associated with the failure of these medical devices upon blood contact, we consider a Tygon coating with the ability to release the natural anticlotting and antibiotic agent, nitric oxide (NO), under simulated physiological conditions. These coatings are prepared by incorporating 20 w/w% S-nitrosoglutathione (GSNO) donor into a Tygon matrix. These films release NO on the order of 0.64 ± 0.5 × 10(-10) mol NO cm(-2) min(-1), which mimics the lower end of natural endothelium NO flux. We use a combination of assays to quantify the amount of GSNO that is found intact at different time points throughout the film soak, as well as monitor the total thiol content in the soaking solution due to any analyte that has leached from the polymer film. We find that a burst of GSNO is released from the material surface within 5 min to 1 h of soaking, which only represents 0.25% of the total GSNO contained in the film. After 1 h of film soak, no additional GSNO is detected in the soaking solution. By further considering the total thiol content in solution relative to the intact GSNO, we demonstrate that the amount of GSNO leached from the material into the buffer soaking solution does not contribute significantly to the total NO released from the GSNO-incorporated Tygon film (<10% total NO). Further surface analysis using SEM-EDS traces the elemental S on the material surface, demonstrating that within 5 min -1 h soaking time, 90% of the surface S is removed from the material. Surface wettability and roughness measurements indicate no changes between the GSNO-incorporated films pre- to postsoak that will be significant toward the adsorption of biological components, such as proteins, relative to the presoaked donor-incorporated film. Overall, we demonstrate that, for a 20 w/w% GSNO-incorporated Tygon film, relatively minimal GSNO leaching is experienced, and the lost GSNO is from the material surface. Varying the donor concentration from 5 to 30 w/w% GSNO within the film does not result in significantly different NO release profiles. Additionally, the steady NO flux associated with the system is predominantly due to localized release from the material, and not donor lost to soaking solution. The surface properties of these materials generally imply that they are useful for blood-contacting applications.

Nitric oxide releasing material adsorbs more fibrinogen.

One mechanism of the failure of blood-contacting devices is clotting. Nitric oxide (NO) releasing materials are seen as a viable solution to the mediation of surface clotting by preventing platelet activation; however, NO's involvement in preventing clot formation extends beyond controlling platelet function. In this study, we evaluate NO's effect on factor XII (fibrinogen) adsorption and activation, which causes the initiation of the intrinsic arm of the coagulation cascade. This is done by utilizing a model plasticized poly(vinyl) chloride (PVC), N-diazeniumdiolate system and looking at the adsorption of fibrinogen, an important clotting protein, to these surfaces. The materials have been prepared in such a way to eliminate changes in surface properties between the control (plasticized PVC) and composite (NO-releasing) materials. This allows us to isolate NO release and determine the effect on the adsorption of fibrinogen, to the material surface. Surprisingly, it was found that an NO releasing material with a surface flux of 17.4 ± 0.5 × 10(-10) mol NO cm(-2) min(-1) showed a significant increase in the amount of fibrinogen adsorbed to the material surface compared to one with a flux of 13.0 ± 1.6 × 10(-10) mol NO cm(-2) min(-1) and the control (2334 ± 496, 226 ± 99, and 103 ±31% fibrinogen adsorbed of control, respectively). This study suggests that NO's role in controlling clotting is extended beyond platelet activation.