ABSTRACT
Natural fiber composites have been extensively studied for structural applications, with recent exploration into their potential for various uses. This study investigates the impact of chemical treatments on the properties of Brazilian jute woven fabric/polyester resin composites. Sodium hydroxide, hydrogen peroxide, and peracetic acid were utilized to treat the jute fabrics, followed by resin transfer molding (RTM) to form the composites. Evaluation included water absorption, flexural strength, tensile strength, and short-beam strength. The alkaline treatment induced changes in the chemical composition of the fibers' surface. Chemical treatments resulted in increased flexural and short-beam strength of the composites, with no significant alterations in tensile properties. The hydrogen peroxide treatment exhibited lower water absorption, suggesting its potential as a viable option for enhancing the performance of these composites.
ABSTRACT
Composites of unsaturated polyester resin (UPR) and cellulose nanofibers (CNFs) obtained from dry cellulose waste of softwood (Pinus sp.) and hardwood (Eucalyptus sp.) were developed. The fiber properties and the influence of the CNFs in the dynamic-mechanical and thermomechanical properties of the composites were evaluated. CNFs with a diameter of 70-90 nm were obtained. Eucalyptus sp. has higher α-cellulose content than Pinus sp. fibers. The crystallinity of the cellulose pulps decreased after grinding. However, high values were still obtained. The chemical composition of the fibers was not significantly altered by the grinding process. Eucalyptus sp. CNF composites had water absorption close to the neat resin at 1 wt% filler. The dynamic-mechanical properties of Eucalyptus sp. CNFs were slightly increased and the thermal stability was improved.