ABSTRACT
This study demonstrates the ability to control the properties of TiO2-CuOx composite layers for photocatalytic applications by using a simple electrophoretic deposition method from isopropanol-based suspension. To obtain uniform layers with a controlled composition, the surfactant sodium lauryl sulfate was used, which influenced the electrophoretic mobility of the particles and the morphology of the deposited layers. The TiO2-CuOx composite layers with different CuOx contents (1.5, 5.5, and 11 wt.%) were obtained. It is shown that the optical band gap measured by UV-VIS-NIR diffuse reflectance spectra. When CuOx is added to TiO2, two absorption edges corresponding to TiO2 and CuOx are observed, indicating a broadening of the photosensitivity range of the material relative to pure TiO2. An open-circuit potential study shows that by changing the amount of CuOx in the composite material, one can control the ratio of free charge carriers (n and p) and, therefore, the catalytic properties of the material. As a result, the TiO2-CuOx composite layers have enhanced photocatalytic activity compared to the pure TiO2 layer: methanol yield grows with increasing CuOx content during CO2 photoreduction.
ABSTRACT
Laser-induced periodic surface structures (LIPSS) can be fabricated in virtually all types of solid materials and show great promise for efficient and scalable production of surface patterns with applications in various fields from photonics to engineering. While the majority of LIPSS manifest as modifications of the surface relief, in special cases, laser impact can also lead to periodic modulation of the material phase state. Here, we report on the fabrication of high-quality periodic structures in the films of phase-change material Ge2Sb2Te5 (GST). Due to considerable contrast of the refractive index of GST in its crystalline and amorphous states, the fabricated structures provide strong spatial modulation of the optical properties, which facilitates their applications. By changing the excitation laser wavelength, we observe the scaling of the grating period as well as transition between formation of different types of LIPSS. We optimize the laser exposure routine to achieve large-scale high-quality phase-change gratings with controllable period and demonstrate their reversible tunability through intermediate amorphization steps. Our results reveal the prospects of fast and rewritable fabrication of high-quality periodic structures for photonics and can serve as a guideline for further development of phase-change material-based optical elements.