Deep Chemical and Physico-Chemical Characterization of Antifungal Industrial Chitosans-Biocontrol Applications.

Five different chitosan samples (CHI-1 to CHI-5) from crustacean shells with high deacetylation degrees (>93%) have been deeply characterized from a chemical and physicochemical point of view in order to better understand the impact of some parameters on the bioactivity against two pathogens frequently encountered in vineyards, Plasmopara viticola and Botrytis cinerea. All the samples were analyzed by SEC-MALS, 1H-NMR, elemental analysis, XPS, FTIR, mass spectrometry, pyrolysis, and TGA and their antioxidant activities were measured (DPPH method). Molecular weights were in the order: CHI-4 and CHI-5 (MW >50 kDa) > CHI-3 > CHI-2 and CHI-1 (MW < 20 kDa). CHI-1, CHI-2 and CHI-3 are under their hydrochloride form, CHI-4 and CHI-5 are under their NH2 form, and CHI-3 contains a high amount of a chitosan calcium complex. CHI-2 and CHI-3 showed higher scavenging activity than others. The bioactivity against B. cinerea was molecular weight dependent with an IC50 for CHI-1 = CHI-2 (13 mg/L) ≤ CHI-3 (17 mg/L) < CHI-4 (75 mg/L) < CHI-5 (152 mg/L). The bioactivity on P. viticola zoospores was important, even at a very low concentration for all chitosans (no moving spores between 1 and 0.01 g/L). These results show that even at low concentrations and under hydrochloride form, chitosan could be a good alternative to pesticides.

Divanillin-Based Aromatic Amines: Synthesis and Use as Curing Agents for Fully Vanillin-Based Epoxy Thermosets.

Bio-based aromatic diamines from vanillin substrate were successfully synthesized and characterized. These amines, i.e., methylated divanillylamine (MDVA) and 3,4-dimethoxydianiline (DMAN), were then tested as curing agents for the design of bio-based epoxy thermosets. The epoxy thermosets obtained from these novel vanillin-based amines exhibited promising thermomechanical properties in terms of glass transition temperature and char residue.

Improvement of the Thermal and Optical Performances of Protective Polydimethylsiloxane Space Coatings with Cellulose Nanocrystal Additives.

This work investigates the possibility of using cellulose nanocrystals (CNCs) as biobased nanoadditives in protective polydimethylsiloxane (PDMS) space coatings, to improve the thermal and optical performances of the material. CNCs produced from wood pulp were functionalized in different conditions with the objective to improve their dispersibility in the PDMS matrix, increase their thermal stability and provide photoactive functions. Polysiloxane, cinnamate, chloroacetate and trifluoroacetate moieties were accordingly anchored at the CNCs surface by silylation, using two different approaches, or acylation with different functional vinyl esters. The modified CNCs were thoroughly characterized by FT-IR spectroscopy, solid-state NMR spectroscopy and thermogravimetric analysis, before being incorporated into a PDMS space coating formulation in low concentration (0.5 to 4 wt %). The cross-linked PDMS films were subsequently investigated with regards to their mechanical behavior, thermal stability and optical properties after photoaging. Results revealed that the CNC additives could significantly improve the thermal stability of the PDMS coating, up to 140 °C, depending on the treatment and CNC concentration, without affecting the mechanical properties and transparency of the material. In addition, the PDMS films loaded with as low as 1 wt % halogenated nanoparticles, exhibited an improved UV-stability after irradiation in geostationary conditions.